Studi Material Biokomposit Untuk Aplikasi Bahan Akustik Dengan Matriks Polyester Berpenguat Serat Alam

Pramono, Muh. Dede (2016) Studi Material Biokomposit Untuk Aplikasi Bahan Akustik Dengan Matriks Polyester Berpenguat Serat Alam. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[img]
Preview
Text
2711100007-Undergraduate_Thesis.pdf - Published Version

Download (4MB) | Preview

Abstract

Penelitian ini dilakukan untuk menganalisa material biokomposit dengan matriks polyester berpenguat serat alam untuk bahan penyerap suara. Permasalahan yang dikaji adalah untuk mengetahui hubungan komposisi serat ampas tebu, serat rami dan serat bambu bermatrik polyester pada komposit terhadap nilai koefisien absorpsi suara (α), kekuatan lenturnya, densitas, ikatan kimia yang terbentuk serta struktur morfologinya. Komposisi yang digunakan adalah 30% serat : 70% matriks. Tujuannya untuk mendapatkan hubungan nilai koefisien absorpsi suara, kuat lentur , densitas, ikatan kimia dan struktur yang terbentuk dengan komposisi yang diberikan serta aplikasinya dalam material penyerap suara yang memenuhi standar ISO 11654. Metode yang digunakan adalah hand lay-up. Metode pengujian berdasarkan standar ASTM E1050, ASTM D790, ASTM C271-99, ASTM E1252 dan ASTM E2809. Dari hasil pengujian didapatkan nilai koefisien absorpsi suara dari ketiga parameter memenuhi standar ISO 11654 dengan nilai koefisien α rata-rata lebih besar dari 0,3 pada frequensi 250-4000 Hz. Dari hasil pengujian lentur didapatkan hasil terbaik pada komposisi dengan dominasi serat tebu dengan 261,66 kg/cm2. Untuk pengujian FTIR, terbukti bahwa tidak terdapat ikatan kimia antara matriks dan penguat ==========================================================================================This study has done to analyze polyester matrix biocomposite material with natural fibers for sound absorbing material. The problem studied was to determine the correlation between the composition of bagasse fiber, flax fiber and bamboo fiber in the biocomposite polyester matrix on the value of the sound absorption coefficient (α), the bending strength, density, chemical bonding and the morfology structure is formed. The composition used is 30% fiber: matrix 70. The goal was to gain exposure value of sound absorption coefficient, flexural strength, density, chemical bonding and morfology structure formed with given composition and their application in sound absorbing material that meets the standards of ISO 11654. The method was hand lay- up. Testing methods based on standard ASTM E1050, ASTM D790, ASTM C271-99, ASTM E1252 and ASTM E2809. From the test results obtained sound absorption coefficient of the three parameters meet ISO 11654 with the value of the average coefficient α greater than 0.3 in the 250-4000 Hz frequency. The best result of bending test was 261.66 kg / cm2. FTIR test proved that there was no chemical bond between the matrix and reinforcement

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.118 Pra s
Uncontrolled Keywords: polyester, rami, serat ampas tebu, serat bambu betung, koefisien absorpsi, kuat lentur, densitas, FTIR, SEM.
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis