Pengaruh Variasi Tekanan Dan Temperatur Warm Compaction Terhadap Struktur Mikro Dan Sifat Mekanik Komposit Cu-10%Sn + 0,5% Zinc Stearate Sebagai Material Peluru Frangible.

Pratama, Nanda Hendra (2016) Pengaruh Variasi Tekanan Dan Temperatur Warm Compaction Terhadap Struktur Mikro Dan Sifat Mekanik Komposit Cu-10%Sn + 0,5% Zinc Stearate Sebagai Material Peluru Frangible. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[thumbnail of 2712100008-Undergraduate_Thesis.pdf]
Preview
Text
2712100008-Undergraduate_Thesis.pdf - Published Version

Download (3MB) | Preview

Abstract

Karakterisasi material peluru frangible dengan pembuatan komposit Cu-10%Sn menggunakan warm compaction telah dilakukan. Pembuatan komposit ini menggunakan metode metalurgi serbuk dengan kadar kemurnian serbuk 99,7%. Metode warm compaction merupakan metode penambahan temperatur pada saat kompaksi. Hal ini bertujuan untuk menghilangkan proses sintering. Prosedur pembuatan komposit ini adalah pencampuran serbuk dengan tujuan menghomogenkan dan kompaksi serbuk dengan menambahkan temperatur. Penelitian ini menggunakan variasi tekanan 300, 400, 500 dan 600 MPa serta variasi temperatur kompaksi 100 dan 200oC. Kedua temperatur menghasilkan nilai densitas yang tertinggi pada tekanan 600 MPa dengan temperatur 100oC dan 200oC berturut – turut adalah 8,33 dan 8,31 g/cm3. Dari hasil pengujian sifat mekanik didapatkan nilai kekerasan maksimum pada tekanan 600 MPa, temperatur 200oC yaitu 195,814 HV dan kekuatan tekan didapatkan nilai maksimum 481,453 MPa pada tekanan 600 MPa, temperatur 200oC. Metode yang digunakan dalam pembuatan komposit Cu10%Sn ini mampu menghasilkan senyawa Cu3Sn dan Cu6Sn5
==========================================================================================Frangible bullet material using Cu10%Sn Composite with warm compaction method characterization has been done. This composite is made by a powder metallurgy method with 99,7% purity. Warm compaction method is a method of adding the temperature at the time of compaction. It aims to eliminate the sintering process. The procedures for making these composites is mixing the powder with the aim of homogenising and compacting the powder by adding temperature. This research use pressure variations 300, 400, 500, 600 MPa and compaction temperature variations 100 and 200OC. The highest density noted on 200OC from compaction temperature variations. It shows 8.33 and 8.31 g/cm3. As the result of mechanical testing, the highest hardness noted on 600 MPa and 200OC. This method confirmed to form Cu3Sn and Cu6Sn5 intermetallics

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.374 Pra d
Uncontrolled Keywords: frangible, metalurgi serbuk, Cu-Sn, warm compaction
Subjects: T Technology > TN Mining engineering. Metallurgy
T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy
T Technology > TS Manufactures > TS699 Powder coating of metals
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 02 Apr 2020 00:55
Last Modified: 02 Apr 2020 00:55
URI: http://repository.its.ac.id/id/eprint/75652