Analisa Perbandingan Laju Korosi Di Lingkungan Laut Dari Hasil Pengelasan Gmaw Pada Sambungan Aluminium Seri 5050 Karena Pengaruh Variasi Kecepatan Aliran Gas Pelindung

Putra, Pandu Damay (2016) Analisa Perbandingan Laju Korosi Di Lingkungan Laut Dari Hasil Pengelasan Gmaw Pada Sambungan Aluminium Seri 5050 Karena Pengaruh Variasi Kecepatan Aliran Gas Pelindung. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 4312100130-Undergraduate_Thesis.pdf]
Preview
Text
4312100130-Undergraduate_Thesis.pdf - Accepted Version

Download (5MB) | Preview

Abstract

Penggunaan aluminium saat ini di dunia industri perkapalan sedang berkembang pesat untuk kapal-kapal cepat karena material ini ringan dan memiliki resistensi terhaap korosi yang baik. Namun pengerjaan panas seperti pengelasan akan mempengaruhi struktur mikro material dan berpengaruh terhadap ketahanan korosi. Pengelasan GMAW (Gas Metal Arc Welding) merupakan pengelasan yang umum digunakan pada material aluminium karena meberikan perlindungan dari oksidasi dengan pencairan gas terhadap material lasan. Penelitian ini bertujuan untuk mengetahui pengaruh dari variasi kecepatan aliran gas pelindung terhadap laju korosi aluminium seri 5050. Variasi kecepatan aliran gas pelindung yang digunakan adalah 15, 20, dan 25 liter/menit. Metode pengujian korosi ini menggunakan bantuan sel tiga elektroda dengan media korosi larutan pengganti air laut dengan salinitas 3,5% yang mengacu pada ASTM G102. Dari pengujian ini didapatkan hasil laju korosi pada pengelasan aluminium dengan kecpatan aliran gas pelindung 15 liter/menit adalah 0,16 mmpy, untuk 20 liter/menit adalah 0,12 mmpy, dan untuk 25 liter/menit adalah 0,08 mmpy. Dari hasil pengujian dapat disimpulkan bahwa semakin besar aliran gas pelindung maka ketahanan material terhadap korosi semakin baik.
=======================================================================================================
Nowadays, the use of aluminum in the world is rapidly growing, in particularly for shipbuilding industry for quick ships because the material is lightweight and has good resistance to corrosion. However, the thermal treatment, such as welding, will affects the microstructure of material and the corrosion resistance of material. GMAW (Gas Metal Arc Welding) is commonly used in the welding of aluminum material because it gives protection from oxidation by a gas liquefaction to the weld metal. This study aims to analyze the effect of variations in shielding gas flow rate against corrosion rate of 5050 series aluminum. Variation of shielding gas flow rate is 15, 20, and 25 liters/minute. Corrosion testing method use the assistance of three-electrode cell with corrosive media is replacement solutions of seawater with 3.5% salinity which refers to ASTM G102 as a standard. This test obtained the rate of corrosion on 5050 series aluminum GMAW welding with shielding gas flow rate of 15 liters/minute is 0.16 mmpy, 20 liters / minute is 0.12 mmpy, and 25 liters / minute is 0.08 mmpy. The test results shall be concluded that the greater shielding of a gas flow rate, hence the corrosion resistance of material is also greater.

Item Type: Thesis (Undergraduate)
Additional Information: RSKe 671.52 Put a
Uncontrolled Keywords: Aluminium Seri 5050, Kecepatan aliran Gas Pelindung, GMAW, Laju Korosi.
Subjects: T Technology > TN Mining engineering. Metallurgy > TN879.6 Welding
Divisions: Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User: Yeni Anita Gonti
Date Deposited: 15 Apr 2020 18:45
Last Modified: 15 Apr 2020 18:45
URI: http://repository.its.ac.id/id/eprint/75764

Actions (login required)

View Item View Item