Studi Eksperimen Pengaruh Komposisi Material Biokomposit Dan Variabel Proses Injeksi Terhadap Kekuatan Tarik Dan Impak

Nugroho, Antonius Danny (2016) Studi Eksperimen Pengaruh Komposisi Material Biokomposit Dan Variabel Proses Injeksi Terhadap Kekuatan Tarik Dan Impak. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[thumbnail of 2113106039-Undergraduate_Thesis.pdf]
Preview
Text
2113106039-Undergraduate_Thesis.pdf - Published Version

Download (4MB) | Preview

Abstract

Pemakaian plastik sangatlah mendominasi pada industri
kecil maupun besar, hal ini dikarenakan sudah banyak produk yang
berbahan baku plastik, diantaranya adalah helm, bodykit motor
maupun mobil, peralatan rumah tangga, dll. Bahan baku plastik
yang mahal serta harus import dari luar negeri memancing kita
untuk memutar otak mencari material terbarukan yang lebih murah
serta ramah lingkungan, salah satunya adalah material
biokomposit. Sekam padi yang dapat digunakan sebagai material
penguat dari biokomposit sangat banyak dijumpai di Indonesia.
Sehingga alangkah baiknya digunakan sebagai campuran dari
material biokomposit daripada tidak terpakai. Pencetakan material
biokomposit menjadi produk jadi tidak lepas dari proses injeksi
molding. Untuk itu dilakukan studi eksperimen penentuan
parameter proses injeksi material biokomposit. Sehingga dengan
parameter yang sesuai dapat meminimalisir cacat serta
meningkatkan sifat mekanis dari material biokomposit.
Pada tugas akhir ini material biokomposit yang digunakan
adalah campuran dari polypropylene (PP), sekam padi dan Maleic
Anhydride Polypropylene (MAPP). Dengan perbandingan
komposisi PP : sekam padi : MAPP berturut-turut adalah 90%wt
PP : 5%wt sekam padi : 5%wt MAPP, 85%wt PP : 10%wt sekam
padi : 5%wt MAPP, 80%wt PP : 15%wt sekam padi : 5%wt MAPP,
75%wt PP : 20%wt sekam padi : 5%wt MAPP. Keempat komposisi
bahan tersebut disimulasikan dengan software Moldflow adviser
2015, agar dapat diketahui parameter proses injeksi yang paling
sesuai dengan mesin injeksi Haitian MA 900/260e. Dengan setting
parameter proses yang didapat dari simulasi, material biokomposit
diinjeksikan untuk menghasilkan spesimen uji tarik ASTM D638-
03 dan impak ASTM D256-04. Spesimen tersebut selanjutnya
dilakukan pengujian tarik dan impak, untuk mengetahui sifat
mekanik dari material biokomposit tersebut. Serta dilakukan uji
SEM (Scanning Electron Microscopy) untuk mengetahui struktur
mikroskopis dari material biokomposit.
Hasil yang didapatkan dari penelitian ini adalah seluruh
komposisi material biokomposit dapat dilakukan proses injeksi.
Material biokomposit dengan komposisi 5%wt sekam padi ; 5%wt
MAPP dan komposisi 10%wt sekam padi ; 5%wt MAPP dapat
digunakan sebagai material alternatif pengganti PP murni.
Dikarenakan memiliki kekuatan tarik dan kekuatan impak berturutturut
29.52 (MPa) ; 28.32 (MPa) dan 3981 (j/m²) ; 3097 (j/m²) yang
mendekati PP murni. Sedangkan material biokomposit dengan
komposisi 15%wt sekam padi ; 5%wt MAPP dan komposisi
20%wt sekam padi ; 5%wt MAPP tidak dapat dijadikan material
alternatif karena sifatnya yang cenderung getas dan tidak tangguh
===============================================================================================
Plastic usages are currently dominating in minor and major
industries, because there are many products which made from
plastic material, such as helmet, motorbike and car’s bodykits,
household appliances, etc. The high-priced imported plastic
material makes us to find a new way to get renewable material with
affordable price and eco-friendly , for example biocomposite
material. Rice husk used as a reinforced material for biocomposite,
which can be easily found in Indonesia. So, it would be good if used
be as a mixture of biocomposite material. Molding process on
biocomposite material into product, are strongly related with
injection molding process. Therefore should be performed
experimental study for determine injection molding parameter
biocomposite material. So, with the best process setting parameter
can minimize the defect found in the product and increase
biocomposite material mechanical properties.
In this final task polypropylene (PP), rice husk and Maleic
Anhydride Polipropylene (MAPP) are used to form biocomposite
material. The formulations are (90%wt PP : 5%wt rice husk :
5%wt MAPP) ; (85%wt PP : 10%wt rice husk : 5%wt MAPP) ;
(80%wt PP : 15%wt rice husk : 5%wt MAPP) and (75%wt PP :
20%wt rice husk : 5%wt MAPP). These four formulations are
simulated with Moldflow adviser 2015 software to get the injection
parameter that fit best with Haitian MA 900/260e injection
machine. These setting parameter to get ASTM D638-03 and ASTM
D256-04 specimens. Biocomposite material specimens are test
with tensile and impact methods to evaluate biocomposite material
mechanical properties. And SEM (Scanning Electron Microscopy)
test to know microscopic structure from biocomposite material.
In this final task, the result have shown that every
biocomposite material composition can be to process injection
molding. Biocomposite material with (90%wt PP : 5%wt rice husk
: 5%wt MAPP) and (85%wt PP : 10%wt rice husk : 5%wt MAPP)
compositions can be used as an alternative material to altenate
pure PP. Because these material have a tensile and impact strength
sequent are 29.52 (MPa) ; 28.32 (MPa) dan 3981 (j/m²) ; 3097
(j/m²) close enough from pure PP. Whereas biocomposite material
with (80%wt PP : 15%wt rice husk : 5%wt MAPP) and (75%wt
PP : 20%wt rice husk : 5%wt MAPP) compositions can not be used
as an alternative material, because have a brittle and not strong
material properties

Item Type: Thesis (Undergraduate)
Additional Information: RSM 620.192 042 23 Nug s
Uncontrolled Keywords: Biokomposit, Maleic Anhydride Polypropylene (MAPP), , Parameter Proses Injeksi, Polypropylene, Sekam Padi, Simulasi
Subjects: T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 28 Jul 2020 00:43
Last Modified: 28 Jul 2020 00:43
URI: http://repository.its.ac.id/id/eprint/76574

Actions (login required)

View Item View Item