Deposisi Elektroforesis Untuk Membuat Lapisan Komposit Hydroxyapatite Pada Kawat Orthodentic

Sari, Nur Shiyama Purnama (2016) Deposisi Elektroforesis Untuk Membuat Lapisan Komposit Hydroxyapatite Pada Kawat Orthodentic. Masters thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2314201019-Master_Thesis.pdf]
Preview
Text
2314201019-Master_Thesis.pdf - Accepted Version

Download (1MB) | Preview

Abstract

Dalam penelitian ini dilakukan study pengaruh penambahan gelatine pada lapisan
komposit HA-SiO2 yang di-coating pada kawat orthodentic dengan menggunakan metode
deposisi elektroforesis. Metode ini digunakan dengan cara menghubungkan sel elektrolisis
dengan power supply pada tegangan 200 V dengan variasi waktu 2, 4, 6, dan 8 menit. Untuk
komposit, konsentrasi HA dan gelatin divariasikan sedangkan konsentrasi SiO2 dibuat tetap.
Konsentrasi HA divariasikan mulai dari 0.5, 1, 1.5, 2, dan 2.5 sedangkan untuk gelatin 0.25,
0.5, 0.75, dan 1. Elektroda karbon berbentuk silinder dipasang sebagai anoda dan kawat
orthodentic sebagai katoda yang diletakkan ditengah-tengah elektroda karbon. Sampel yang
telah terlapisi oleh komposit HA-SiO2 dan gelatin selanjutnya dipanaskan pada suhu 80 oC
selama 24 jam. Uji SEM menunjukkan bahwa adanya gelatin mampu meningkatkan sifat
fisik dari komposit HA-SiO2. Sedangkan dari uji kualitatif dengan bantuan selotip
menunjukkan bahwa adanya gelatin mampu meningkatkan daya lekat coating. Tingginya
daya rekat coating komposit HA-SiO2 pada permukaan kawat mampu meningkatkan
ketahanan korosi. Hasil EDAX dan FTIR menunjukkan bahwa gelatin mampu mengikat
komposit HA-SiO2 pada permukaan kawat orthodentic dengan ditemukannya unsur-unsur
dan gugus fungsi dari komposit HA-SiO2.
==================================================================================================================
In this research conducted study the effect of the addition of gelatine in the composite
layer in the HA-SiO2 and gelatin coating on the orthodentic wire using electrophoretic
deposition. This method is used by connecting the electrolysis cell with a power supply at a
voltage of 200 V with a time variation of 2, 4, 6, and 8 minutes. For the composites, the
concentration of HA and gelatin varied while the concentration of SiO2 is made permanent.
The concentration of HA varied from 0.5, 1, 1.5, 2, and 2.5 while for gelatin 0.25, 0.5, 0.75,
and 1. The cylindrical carbon electrodes fitted as an anode and a cathode orthodentic wire
that is placed in the midst of a carbon electrode. Samples were coated by a composite HASiO2 and gelatin further heated at a temperature of 80 ° C for 24 hours. SEM test shows that
the gelatin can improve the physical properties of composite HA-SiO2. While the qualitative
test with the help of masking tape showed that the gelatin can improve adhesion coating
EDAX and FTIR results showed that the gelatin is able to bind HA-SiO2 composite on the
surface of the wire orthodentic with the discovery of the elements and functional groups of
HA-SiO2 composite.

Item Type: Thesis (Masters)
Additional Information: RTK 660.297 2 Sar d
Uncontrolled Keywords: Hydroxyapatite, Silicon dioxide, Gelantine, Deposisi elektroforesis
Subjects: Q Science > QP Physiology > QP519.9.E434 Electrophoresis.
Divisions: Faculty of Industrial Technology > Chemical Engineering > 24101-(S2) Master Thesis
Depositing User: ansi aflacha
Date Deposited: 29 Jul 2020 04:02
Last Modified: 29 Jul 2020 04:02
URI: http://repository.its.ac.id/id/eprint/76641