Review : Pengaruh Proses Alkalisasi Serat Terhadap Morfologi, Struktur Dan Sifat Absorpsi Suara Komposit Serat Alam

Apriliani, Nurul Qomariyah (2020) Review : Pengaruh Proses Alkalisasi Serat Terhadap Morfologi, Struktur Dan Sifat Absorpsi Suara Komposit Serat Alam. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02511640000013-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Kepopuleran serat alam sebagai material yang inovatif menjadi faktor penting dalam peluang pengembangan teknik penyerapan suara dari material berpori menggunakan serat alam. Tujuan dari review ini adalah untuk mengetahui pengaruh variasi konsentrasi, temperatur dan waktu pada proses alkalisasi serat terhadap terhadap morfologi, struktur dan sifat absorpsi suara dari komposit serat alam. Serat alam memiliki beberapa kelemahan akibat kandungan non selulosa yang dapat melemahkan ikatan antar fasa matriks dan penguat pada komposit. Sehingga perlakuan alkalisasi dengan NaOH pada serat alam dilakukan dengan tujuan untuk memperbaiki ikatan antar fase penguat dan fase matriks pada komposit. Hasil review menunjukkan bahwa pada range 2-5wt% NaOH pada rentang 25 - 60°C dengan waktu pemrosesan selama 1-12 jam menunjukkan morfologi dan struktur serat yang lebih bersih dan permukaan yang kasar dengan hilangnya kandungan pengotor pada serat. Nilai koefisien absorpsi suara pada komposit serat alam semakin naik setelah serat diberi perlakuan alkalisasi dengan konsentrasi 2-5% NaOH. Didapati bahwa nilai koefisien penyerapan suara dari serat alam mendekati 1 dalam rentang frekuensi rendah 1,6-3,250 kHz. ================================================================================================================== The popularity of natural fibers as innovative materials has become an important factor in the development of sound absorption techniques from porous materials using natural fibers. The purpose of this paper review is to determine the effect of various concentrations of sodium hydroxide, temperature, and time of alkali treatment on the morphology, structure, and sound absorption performance of natural fiber composites. Natural fibers have some disadvantages due to non-cellulose content which can weaken the interfacial bonding between the matrix and reinforcing phases in the composite. So that the alkalization treatment with NaOH in natural fibers is done to improve the bond between the reinforcing phase and the matrix phase of the composite. The review results show that in the range of 2-5wt% NaOH in the range of 25 - 60 ° C with the processing time of 1-6 hours, the morphology and structure of the fiber are cleaner and the surface is rough with the loss of impurities in the fiber. The sound absorption coefficient on natural fiber composites increased after the fibers were treated with 2-5% NaOH concentrates. It was found that the sound absorption coefficient of the treated natural fibers was close to 1 the low-frequency range of 1.6-3,250 kHz.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Alkalisasi, Serat alam, Morfologi, Struktur, Sifat absorpsi suara, Alkalisasi, Serat alam, Morfologi, Struktur, Sifat absorpsi suara
Subjects: Q Science
Q Science > QC Physics
Q Science > QC Physics > QC173.4.C63 Composite materials
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Nurul Qomariyah Apriliani
Date Deposited: 13 Aug 2020 08:42
Last Modified: 13 Aug 2020 08:42
URI: http://repository.its.ac.id/id/eprint/77933

Actions (login required)

View Item View Item