Aplikasi Sintesis Tio2 Dengan Prekursor Ticl3 Sebagai Self Cleaning Pada Cat Tembok Dengan Dispersant Peg 6000

Wahyuningtyas, Rizkyanti Desy (2014) Aplikasi Sintesis Tio2 Dengan Prekursor Ticl3 Sebagai Self Cleaning Pada Cat Tembok Dengan Dispersant Peg 6000. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[thumbnail of 2410100022-Undergraduate_Thesis.pdf]
Preview
Text
2410100022-Undergraduate_Thesis.pdf - Published Version

Download (1MB) | Preview

Abstract

Telah diaplikasikan sintesis nanopartikel TiO2 dari prekursor TiCl3 dengan fase anatase dan rutile pada komposisi 1%, 1,5%, dan 2% sebagai self cleaning pada cat tembok menggunakan polietilen glikol (PEG) 6000 sebagai dispersant. Ukuran partikel yang didapat untuk fase anatase adalah 34,45 nm dan 60,65 nm untuk fase rutile. Pengujian self cleaning menggunakan dua macam pengotor yaitu lumpur dan tinta sepidol warna hitam. Dari pengujian FTIR, masih menunjukkan absorbansi pada bilangan gelombang tertentu yang merupakan karakteristik PEG. Pengolahan citra menggunakan ImageJ digunakan untuk menghitung luas area pengotor, prosentase sisa pengotor dan distribusi TiO2. Untuk mengetahui distribusi TiO2 pada cat dilakukan pengujian menggunakan Scanning Electron Microscopes (SEM). Hasil pengolahan citra menunjukkan 2% TiO2 dengan perbandingan anatase : rutile = (90:10) memiliki luas area pengotor paling kecil untuk pengotor lumpur dan 2% TiO2 dengan perbandingan anatase : rutile = (95:5) untuk pengotor tinta sepidol warna hitam
===================================================================================================
Has been applied to the synthesis of TiO2 nanoparticles from precursors TiCl3 with rutile and anatase phase, on the composition of 1%, 1,5% and 2% as self cleaning wall paint using polyethylene glycol (PEG) 6000 as a dispersant. The size of the particles obtained for anatase phase is 34, 45 nm and rutile phase for 60,65 nm. Self cleaning test using two kinds of pollutant that mud and ink markers in black color. From FTIR characterizations show wave number absorbance indicating characteristic peaks of PEG. Image processing using ImageJ is used to calculate the area of pollutant, percentage of TiO2 pollutant and distribution. Scanning Electron Microscopes (SEM) using to find the calculated area of pollutant and distribution of TiO2. Image processing result show that 2% TiO2 with ratio of anatase : rutile = (90:10) has the minimum mud pollutant area and 2% TiO2 with ratio anatase : rutile = (95:5) for ink marker pollutan area

Item Type: Thesis (Undergraduate)
Additional Information: RSF 667.9 Wah a
Uncontrolled Keywords: anatase, PEG, rutile, self cleaning, TiO2
Subjects: T Technology > TS Manufactures > TS699 Powder coating of metals
Divisions: Faculty of Industrial Technology > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 07 Jan 2021 03:06
Last Modified: 07 Jan 2021 03:06
URI: http://repository.its.ac.id/id/eprint/82373

Actions (login required)

View Item View Item