Studi Eksperiment Pengaruh Metal Transfer Pada kekuatan Sambungan Las Aluminium 5083 Dengan Proses GMAW

Aryasatyo, Alvin Tino (2021) Studi Eksperiment Pengaruh Metal Transfer Pada kekuatan Sambungan Las Aluminium 5083 Dengan Proses GMAW. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 04311640000100_Undergraduate_Thesis.pdf] Text
04311640000100_Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2023.

Download (7MB) | Request a copy

Abstract

Aluminium 5083 banyak digunakan untuk pembuatan kapal kecil, seperti kapal patroli atau kapal perang. Dalam proses pembuatan sebuah konstruksi maupun bangunan lepas pantai tidak terlepas dari proses pengelasan. Salah satu metode pengelasan yang sering dipakai oleh masyarakat umum, yaitu metode GMAW. Dalam pengelasan sendiri memiliki beberapa faktor pengaruh perubahan hasil dari pengelasan. Metal transfer adalah salah satu perlakuan pengelasan yang terjadi adanya pengaruh dari perubahan arus dan tegangan listrik yang diberikan pada elektroda, penentuan tegangan dan arus listrik pada nilai tertentu berpengaruh pada lelehan yang terjadi pada elektroda. Perlakuan yang diberikan tersebut dapat mempengaruhi kondisi sambungan las dari material las itu sendiri. Dengan adanya masalah tersebut perlu adanya penelitian lebih lanjut terkait pengaruh perbedaan perlakuan metal transfer pada pengelasan, dengan variasi yang digunakan yaitu pada arus dan tegangan listrik yang digunakan terhadap pengaruh kekuatan pada sambungan las, serta spatter yang terjadi pada pengelasan. Variasi yang digumakam pada penelitian ini adalah Short Circuit (Ampere 116, Volt Range 16), Short Circuit (Ampere 124, Volt Range 16), Globular (Ampere 116, Volt Range 24), Globular (Ampere 124, Volt Range 24). Dalam hasil pengujian pada pengelasan tersebut , variasi Globular (Ampere 116, Volt Range 24) memliki rata-rata nilai kekuatan pada uji tarik terbesar yield strength 160.37 MPa & ultimate strength 220.2 Mpa. Spatter terjadi pada variasi Short Circuit (Ampere 116, Volt Range 16) dan Globular (Ampere 116, Volt Range 24) tidak menimbulkan cacat dikarenakan spatter masih dapat dibersihkan.
======================================================================================================
Aluminum 5083 is widely used for the manufacture of small ships, such as patrol boats
or warships. In the process of making a construction or an offshore building is
inseparable from the welding process. One of the welding methods that is often used
by the general public, namely the GMAW method. In welding itself has several factors
influence changes in the results of welding. Metal transfer is one of the welding
treatments that occur the influence of changes in current and electrical voltage given to
electrodes, determination of voltage and electric current at a certain value affects the
melting that occurs in electrodes. The treatment given can affect the weld connection
condition of the welding material itself. With this problem, there needs to be more
research related to the influence of differences in metal transfer treatment on welding,
with variations used in current and electrical voltage used against the influence of force
on welding joints, as well as spatters that occur in welding. The variations recorded in
this study are Short Circuit (Ampere 116, Volt Range 16), Short Circuit (Ampere 124,
Volt Range 16), Globular (Ampere 116, Volt Range 24), Globular (Ampere 124, Range
Volt 24). In the test results on the welding, globular variations (Ampere 116, Volt
Range 24) have an average strength value on the largest tensile test yield strength of
160.37 MPa &ultimate strength 220.2 Mpa. Spatters occur in short circuit variations
(Ampere 116, Volt Range 16) and Globular (Ampere 116, Volt Range 24) do not cause
defects because spatters can still be cleaned.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: GMAW, aluminium 5083, metal transfer, uji tarik, spatter.
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TA Engineering (General). Civil engineering (General) > TA492.W4 Welded joints
T Technology > TS Manufactures > TS227 Welding.
Divisions: Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User: Alvin Tino Aryasatyo
Date Deposited: 17 Aug 2021 21:05
Last Modified: 17 Aug 2021 21:05
URI: http://repository.its.ac.id/id/eprint/87028

Actions (login required)

View Item View Item