Pengaruh Medan Listrik Pada Sintesa Nanopartikel Lignin Berbasis Sabut Kelapa Sebagai Material Anti UV

Sari, Diana Novita (2021) Pengaruh Medan Listrik Pada Sintesa Nanopartikel Lignin Berbasis Sabut Kelapa Sebagai Material Anti UV. Masters thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 02211950010003-Master_Thesis.pdf] Text
02211950010003-Master_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2023.

Download (6MB) | Request a copy

Abstract

Lignin merupakan solusi yang menjanjikan untuk diaplikasikan dalam kosmetik sebagai sunscreen. Sejauh ini penelitian sudah dikembangkan, namun masih terbatas pada sintesa lignin menggunakan bahan yang tidak ramah lingkungan, berbahaya bagi kulit serta ukuran partikelnya masih besar. Oleh karena itu, pada penelitian ini dikembangkan sintesa lignin menggunakan pelarut yang tidak berbahaya bagi kulit yaitu dengan etanol dan pembuatan partikelnya menggunakan metode spray drying yang dimodifikasi adanya medan listrik sehingga didapat nanopartikel lignin. Penelitian ini bertujuan untuk mengembangkan metode pembentukan nanopartikel lignin berbasis sabut kelapa dengan metode spray drying yang dimodifikasi dengan bantuan medan listrik untuk aplikasi sunscreen. Variabel yang digunakan pada penelitian ini yaitu suhu pemanasan dan tegangan. Berdasarkan hasil eksperimen, didapati untuk variabel suhu pemanasan dan tegangan yang memberikan ukuran partikel terkecil dengan
diameter 315 nm dan nilai SPF tertinggi bernilai 40,00 yaitu pada suhu pemanasan 500oC dan tegangan 20 kV, dimana suhu pemanasan dan tegangan yang tinggi dapat menurunkan ukuran partikel dan menaikkan nilai SPF.
=====================================================================================================
Lignin is a promising solution to be applied in cosmetics as a sunscreen. So far, research has been developed, but it is still limited to the synthesis of lignin using materials that are not environmentally friendly, harmful to the skin and the particle size is still large. Therefore, in this research, the synthesis of lignin was
developed using a solvent that is not harmful to the skin, namely ethanol and the manufacture of the particles using the spray drying method modified by an electric field to obtain lignin nanoparticles. This study aims to develop a method of forming coir fibers-based lignin nanoparticles using a modified spray drying method with the help of an electric field for sunscreen application. The variables used in this study are heating temperature and voltage. Based on the experimental results, it was found that the heating temperature and voltage variables gave the smallest particle size with a diameter of 315 nm and the highest SPF value of 40.00, namely at a heating temperature of 500oC and a voltage of 20 kV, where high heating temperature and voltage can reduce particle size and increase the SPF value.

Item Type: Thesis (Masters)
Uncontrolled Keywords: Lignin, Medan Listrik, Sunscreen, Electric Field
Subjects: Q Science > QD Chemistry > QD115 Electrochemical analysis
T Technology > TP Chemical technology
T Technology > TS Manufactures > TS176 Manufacturing engineering. Process engineering (Including manufacturing planning, production planning)
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Chemical Engineering > 24101-(S2) Master Thesis
Depositing User: Diana Novita Sari
Date Deposited: 22 Aug 2021 02:14
Last Modified: 22 Aug 2021 02:14
URI: http://repository.its.ac.id/id/eprint/88307

Actions (login required)

View Item View Item