Studi Pembuatan Nanofluida Silika dengan Metode Karbonasi Untuk Enhanced Oil Recovery (EOR)

Sekaringgalih, Ratri (2021) Studi Pembuatan Nanofluida Silika dengan Metode Karbonasi Untuk Enhanced Oil Recovery (EOR). Masters thesis, Institut Teknologi Sepuluh November.

[thumbnail of 02211950010012-Master_Thesis.pdf] Text
02211950010012-Master_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2023.

Download (2MB) | Request a copy
[thumbnail of 02211950010012-Master_Thesis.pdf] Text
02211950010012-Master_Thesis.pdf
Restricted to Repository staff only

Download (2MB) | Request a copy
[thumbnail of 02211950010012-Master_Thesis.pdf] Text
02211950010012-Master_Thesis.pdf
Restricted to Repository staff only

Download (2MB) | Request a copy
[thumbnail of 02211950010012-Master_Thesis.pdf] Text
02211950010012-Master_Thesis.pdf
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mempelajari pengaruh laju alir dan konsentrasi larutan natrium silikat terhadap parameter kestabilan nanofluida silika, dan mengetahui adanya pengaruh penambahan surfaktan (sodium lauryl sulfate) terhadap parameter kestabilan nanofluida silika. Prosedur pada penelitian ini yaitu pembuatan larutan prekursor untuk proses karbonasi. Kemudian larutan prekursor mengalami proses karbonasi dengan bantuan diffuser yang mengalirkan gas CO2, proses ini terjadi pada suhu ambient dan tekanan 1 atm dengan variasi konsentrasi larutan natrium silikat serta laju alir feed. Setelahnya dilakukan pengambilan sampling larutan setiap 5 menit untuk diukur pH, proses ini dilakukan sampai diperoleh larutan dengan pH konstant. Proses karbonasi terlebih dahulu dilakukan secara batch, tujuannya adalah untuk menemukan kondisi terbaik, yang kemudian digunakan untuk acuan pada penerapan proses secara kontinyu. Dari hasil yang diperoleh menunjukkan bahwa semakin kecil laju alir feed maka penurunan nilai pH pada tiap titik pengamatan menunjukkan nilai yang semakin besar. Hal ini karena apabila laju alirnya kecil maka kecepatan kontak gas CO2 dengan larutan untuk membuat kondisi konstan akan semakin lama. Pengaruh dari konsentrasi, semakin tinggi konsentrasi sodium silikat yang digunakan maka nilai pH konstan ditunjukkan dengan nilai yang semakin meningkat. Kondisi terbaik nanofluida silika-surfaktan diperoleh pada konsentrasi 0,5% dan laju alir 8 ml/detik. Pada proses EOR sistem nanofluida silika-surfaktan dapat meningkatkan %perolehan kembali dan mengubah wettability permukaan.
======================================================================================================
This study aims to study the effect of flow rate and concentration of sodium silicate solution on the stability parameters of silica nanofluids, and determine the effect of adding surfactant (sodium lauryl sulfate) to the stability parameters of silica nanofluids. The procedure in this research is the preparation of a precursor solution for the carbonation process. Then the precursor solution undergoes a carbonation process with the help of a diffuser that flows CO2 gas, this process occurs at ambient temperature and pressure of 1 atm with variations in the concentration of sodium silicate solution and feed flow rate. After that, a sample of the solution was taken every 5 minutes to measure the pH, this process was carried out until a solution with a constant pH was obtained. The carbonation process is first carried out in batches, the aim is to find the best conditions, which are then used as a reference for the application of the process continuously. From the results obtained indicate that the smaller the feed flow rate, the decrease in the pH value at each observation point shows a greater value. This is because if the flow rate is small, the contact speed of CO2 gas with the solution to make the condition constant will be longer. The effect of concentration, the higher the concentration of sodium silicate used, the constant pH value is indicated by an increasing value. The best condition of silica-surfactant nanofluid was obtained at a concentration of 0.5% and a flow rate of 8 ml/second. In the EOR process, the silica-surfactant nanofluid system can increase % recovery and change the surface wettability

Item Type: Thesis (Masters)
Uncontrolled Keywords: nanofluida silika, natrium lauril sulfat, karbonasi, dan enhanced oil recovery, nanofluid silica, sodium lauryl sulfate, carbonation
Subjects: Q Science > QC Physics
T Technology > TP Chemical technology
T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles.
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Chemical Engineering > 24101-(S2) Master Thesis
Depositing User: Ratri Sekaringgalih
Date Deposited: 22 Aug 2021 02:09
Last Modified: 22 Aug 2021 02:09
URI: http://repository.its.ac.id/id/eprint/88312

Actions (login required)

View Item View Item