Simulasi Pengaruh Ketebalan Perovskite Terhadap Nilai Efisiensi Pada Sel Surya Perovskite

Paramita, Maria Stella Widya (2021) Simulasi Pengaruh Ketebalan Perovskite Terhadap Nilai Efisiensi Pada Sel Surya Perovskite. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 01111740000091_UNDERGRADUATE_THESIS.pdf - Accepted Version Restricted to Repository staff only until 1 October 2023. Download (1MB) | Request a copy

Abstract

Dalam sel surya berbasis perovskite saat ini masih banyak berfokus pada sintesis, karakterisasi dan fabrikasi. Namun, masih banyak penelitian yang dilakukan dimana diperoleh nilai efisiensinya masih sekitar ~20%. Untuk itu dalam penelitian ini dilakukan simulasi sel surya berbasis perovskite dengan menggunakan perangkat lunak GPVDM dengan variasi ketebalan lapisan perovskite dan lapisan material CsI guna memperoleh nilai efisiensi yang lebih tinggi dibandingkan dengan penelitian sebelumnya yang diperoleh nilai efisiensinya sebesar 17,26% dengan susunan lapisan yang digunakan yaitu FTO-TiO2-Perovskite-CsI-SpiroMeOTAD-Au dengan ketebalan FTO sebesar 500nm, lapisan TiO2 setebal 40 nm, ketebalan perovskite sebesar 300 nm, lapisan CsI dengan tebal 5 nm dan lapisan Au dengan ketebalan 100 nm. Tetapi pada penelitian ini untuk lapisan perovskite dan lapisan CsI menggunakan variasi dengan masing-masing rentang 100 nm hingga 1000 nm dan 10 nm hingga 100 nm dimana dengan menggunakan susunan lapisan yang sama. Setelah dilakukan simulasi sel surya berbasis perovskite tersebut, diperoleh nilai efisiensi dengan rentang 11%~24% pada semua variasi yang digunakan. Untuk variasi ketebalan perovskite nilai efisiensi tertinggi sebesar 23,81% yang diperoleh pada ketebalan perovskite sebesar 900 nm sedangkan variasi ketebalan CsI nilai efisiensi tertinggi sebesar 18,57% yang diperoleh pada ketebalan lapisan CsI setebal 95 nm.
=====================================================================================================
Perovskite solar cell materials nowadays focus on synthesis, characterization, and fabrication. However, there are still many studies conducted where the efficiency value is still around ~20%. For that reason, in this research a perovskite-based solar cell simulation was carried out using GPVDM software with variations of the thickness of the perovskite layer and CsI material in order to obtain a higher efficiency value compared to previous research which obtained an efficiency value 17.26% with the layer arrangement that used FTO-TiO2-Perovskite-CsI-SpiroMeOTAD-Au with a FTO thickness 500 nm, a TiO2 layer with thickness 40 nm, a perovskite layer with thickness 300 nm, a CsI layer with thickness 5 nm and an Au layer with the thickness 100 nm. However, in this research the perovskite layer and CsI layer used variations with each range from 100 nm to 1000 nm and 10 nm to 100 nm where the same layer arrangement that used. After simulated the perovskite solar cells, the efficiency values obtained in the range of 11%~24% in all variations. For variations in the thickness of perovskite, the highest efficiency value of 23.81% was obtained at a perovskite thickness 900 nm, while for variations in thickness of CsI the highest efficiency value 18.57% was obtained at a thickness of CsI layer as thick as 95 nm.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	the efficiency, thickness, perovskite, solar cell, efisiensi, ketebalan, sel surya
Subjects:	T Technology > TJ Mechanical engineering and machinery > TJ810.5 Solar energy T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2960 Dye-sensitized solar cells. Solar batteries. Solar cells
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Maria Stella Widya Paramita
Date Deposited:	26 Aug 2021 08:03
Last Modified:	26 Aug 2021 08:03
URI:	http://repository.its.ac.id/id/eprint/89164