Kinerja Membran Geopolimer dari Metakaolin Dalam Pemisahan Metilen Biru Dari Larutan: Pengaruh Konsentrasi Awal Metilen Biru

Milati, Milati (2021) Kinerja Membran Geopolimer dari Metakaolin Dalam Pemisahan Metilen Biru Dari Larutan: Pengaruh Konsentrasi Awal Metilen Biru. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 01211740000026-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2023. Download (2MB) | Request a copy

Abstract

Membran geopolimer disintesis dari metakaolin sebagai sumber
aluminosilikat yang diaktifkan dengan larutan NaOH dan Na2SiO3. Pada
tahap sintesis geopolimer, dilakukan penambahan hidrogen peroksida
sebagai zat pembentuk pori. Pori pada membran geopolimer terbentuk
sebagai akibat dari dekomposisi hidrogen peroksida menjadi gas oksigen
dan air. Keberadaan pori-pori membran menyebabkan geopolimer yang
dihasilkan mempunyai kuat tekan rendah yaitu 4,24 MPa. Jumlah
hidrogen peroksida yang ditambahkan adalah 3% dari berat total bahan
baku membran geopolimer serta konsentrasi awal larutan umpan MB
adalah 10, 20 dan 30 ppm. Pemisahan pewarna metilen biru (MB)
menggunakan membran geopolimer dengan metode filtrasi telah berhasil
dilakukan. Semakin besar konsentrasi awal pewarna MB yang digunakan
sebagai larutan umpan, semakin kecil nilai fluks yang dihasilkan yang
diperkirakan terjadi sebagai akibat dari penyumbatan pori-pori membran
oleh molekul metilen biru yang teradsorpsi oleh permukaan membran.
Rejeksi metilen biru tertinggi untuk masing-masing konsentrasi adalah
74,90; 78,00 dan 87,37 %.
======================================================================================================
Geopolymer membrane synthesized from metakaolin as a source of
aluminosilicate activated by NaOH and Na2SiO3 solutions. In the
geopolymer synthesis stage, hydrogen peroxide is added as a pore�forming agent. The pores are formed as a result of the decomposition of
hydrogen peroxide into oxygen gas and water. The presence of membrane
pores causes the geopolymer to have a low compressive strength (4.24
Mpa). The amount of hydrogen peroxide additive was 3% of the total
weight of the geopolymer membrane’s raw material and the initial
concentration of the MB in feed solution was 10, 20 and 30 ppm. This
research used hydrogen peroxide with an additional weight of 3% of the
total weight of the geopolymer membrane raw material and the initial
concentration of the MB feed solution was 10, 20 and 30 ppm.. The
separation of methylene blue (MB) using a geopolymer membrane with
the filtration method has been done successfully. Higher initial
concentration of MB in the feed solution causes the decrease in flux,
probably due to methylene blue fouling on the surface of the geopolymer
membrane. The highest rejection for each concentration the membrane is
74,90; 78,00 dan 87,37 %.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Metakaolin, Membran Geopolimer, Metilen biru, Filtrasi, Adsorpsi, Metakaolin, Geopolymer Membrane, Methylene Blue, Filtration, Adsorption.
Subjects:	Q Science > QD Chemistry > QD181.S6 A4 Aluminum silicates
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	MILATI MILATI
Date Deposited:	28 Aug 2021 03:06
Last Modified:	29 Mar 2022 02:54
URI:	http://repository.its.ac.id/id/eprint/90311

Actions (login required)

View Item