Analisis Perbandingan Sifat Mekanik Pengelasan Stainless Steel SS304 Menggunakan GMAW, FCAW & SMAW

Pramudana, Muhammad Hafidh (2022) Analisis Perbandingan Sifat Mekanik Pengelasan Stainless Steel SS304 Menggunakan GMAW, FCAW & SMAW. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 04311840000048-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2024. Download (1MB) | Request a copy

Abstract

Kapal dan Bangunan Lepas Pantai merupakan salah satu diantara beberapa benda dalam industri kelautan yang dapat dilakukan pengelasan. Material stainless steel 304 sering dijumpai di bangunan kapal khususnya pada bagian yang sering terkena pegangan langsung menggunakan 3 macam metode pengelasan diantaranya adalah GMAW, FCAW dan SMAW yang kemudian akan dilakukan pengelasan pada bahan Stainless Steel 304 untuk mendapatkan hasil berupa perbandingan sifat mekanik dari hasil pengelasan tersebut, sedangkan untuk sifat mekanik yang dituju berupa hasil uji kekerasan, uji tarik dan uji bending. Pada pengujian ini hasil pengujian kekerasan terbaik adalah hasil pengelasan GMAW yaitu mempunyai rata-rata senilai 264 HVN. Sedangkan untuk pengujian tarik terbaik adalah hasil pengelasan SMAW mempunyai Beban ultimate yang diperoleh oleh proses pengelasan SMAW yaitu sebesar 34153 N. Hasil beban yield juga dimiliki paling tinggi oleh pengelasan SMAW yang nantinya berpengaruh kepada elongasi material tertinggi juga dimiliki oleh pengelasan SMAW yaitu sebesar 55 %.Hasil pengujian tekuk semua spesimen mempunyai hasil yang baik dan memenuhi Acceptance Criteria, crack sebesar ±1 mm hanya terjadi di bagian face bending proses las GMAW. Dengan menggunakan Metode Perbandingan Eksponensial (MPE) dapat ditarik kesimpulan proses pengelasan terbaik untuk material stainless steel 304 adalah proses pengelasan GMAW. Walaupun secara data mempunyai selisih hasil yang sangat sedikit, namun proses pengelasan GMAW mempunyai hasil uji yang lebih baik tertutama pada hasil uji kekerasan.
================================================================================================
Marine vessels and offshore structures are one of many examples in marine industry which apply welding technology. Stainless steel 304 is one of the most common material that used for building marine vessels, especially in the areas that have the highest contact rate with human and liquids. GMAW, FCAW, and SMAW methods will be used to weld Stainless Steel 304 in order to compare the mechanical properties of the welds, the mechanical properties that addressed in this study are the hardness test, the tensile test, and the bending test. The result of hardness test points that GMAW is the best method with the rate of 264 HVN. For the tensile test, the results points that SMAW is the best method with ultimate force of 34153 N. The yield test results will affect the material elongation, with 55% of material elongation SMAW found to be the best method for the yield test. The result of the bending test shows that all the methods have meet the Acceptance Criteria, ±1 mm crack was only found in face bending process from GMAW method. In conclusion, utilizing the MPE method points that GMAW is the best method for welding Stainless Steel 304 materials. Despite the minimum result differences between the methods, GMAW have better quality of hardness test.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Pengelasan, Material Stainless steel 304, Sifat Mekanik, GMAW, FCAW, SMAW, Welding, Mechanical Properties
Subjects:	T Technology > TC Hydraulic engineering. Ocean engineering > TC1665 Offshore structures--Materials.
Divisions:	Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User:	Muhammad Hafidh Pramudana
Date Deposited:	02 Feb 2022 06:57
Last Modified:	01 Nov 2022 04:09
URI:	http://repository.its.ac.id/id/eprint/92648

Actions (login required)

View Item