Analisis Pengaruh 3-Methacryloxypropyl Trimethoxysilane sebagai Coupling Agent terhadap Morfologi dan Sifat Mekanik Al2O3/ZrSiO4 untuk Aplikasi Implan Mahkota Gigi

Stany, Ferginia (2021) Analisis Pengaruh 3-Methacryloxypropyl Trimethoxysilane sebagai Coupling Agent terhadap Morfologi dan Sifat Mekanik Al2O3/ZrSiO4 untuk Aplikasi Implan Mahkota Gigi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000091-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2024. Download (4MB) | Request a copy

Abstract

Biomaterial implan gigi menjadi alternatif dalam mengatasi fenomena kerusakan gigi yang kerap terjadi. Alumina dengan kepadatan dan kemurnian yang tinggi, kombinasi ketahanan korosi dan kompatibilitas yang baik, ketahanan aus dan kekuatan yang tinggi dan zirkon dengan ketangguhan yang baik mampu menghasilkan biomaterial komposit yang baik dalam aplikasi implan gigi. Modifikasi permukaan pada zirkon dilakukan dengan penambahan 3-Methacryloxypropyl Trimethoxysilane sebagai coupling agent dengan variasi penambahan sebesar 0.5%, 1.5%, dan 3% pada rasio Al2O3/ZrSiO4 80:20, 85:15, 90:10. Penelitian ini menunjukan bahwa penambahan 3-MPS sebagai coupling agent membentuk ikatan siloxane yang mampu memperbaiki ikatan antara matriks dan filler dalam hal ini adalah Al2O3/ZrSiO4. Bonding yang lebih baik berkaitan dengan sifat mekanik yang dihasilkan. Peningkatan persentase penambahan 3-MPS mampu memperbaiki sifat termal dan nilai kekerasan pada Al2O3/ZrSiO4 dibuktikan dengan penambahan 3% MPS memperkecil persentase penurunan massa menjadi sebanyak 1% dan nilai kekerasan tertinggi sebesar 10,74 GPa. Namun, penambahan 3-MPS pada kadar tersebut belum cukup untuk meningkatkan nilai kuat tekan pada 20 wt% Al2O3/ZrSiO4 dengan nilai kuat tekan yang diperoleh pada setiap persentasenya ialah 23,74, 46,73, dan 50,69 MPa.
=====================================================================================================
Biomaterial as dental implants can be used as an alternative by replacing the function of the damaged body tissues. Alumina with the high density and purity, good corrosion resistance and compatibility, high wear resistance and strength properties and zircon with the good toughness properties are able to produce good composite biomaterial for dental implant application. Surface modification was carried out on zircon by adding 3-Methacryloxypropyl Trimethoxysilane as an coupling agent with variation 0.5, 1.5, and 3% in Al2O3/ZrSiO4 with ratio 90:10, 85:15, and 80:20. This research shows that the addition of 3-MPS formed siloxane on zircon surface so be able to formed better interfacial bonding between the matrix and filler, Al2O3/ZrSiO4. The good bonding lead to better mechanical properties. The increasing percentage of 3-MPS generate a better thermal shown by decreasing the mass reduction into 1% and hardness value of 10.74 GPa. However, the addition of 3-MPS at these percentage was not sufficient to form a better compressive strength of Al2O3/ZrSiO4 with the compressive strength values obtained 23.74 for 0.5%, 46.73% for 1.5% and 50.69% for 3% of 3-MPS

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	3-MPS, Alumina, Coupling Agent, Dental Implant, Zircon, 3-MPS, Alumina, Coupling Agent, Implan Gigi, Zirkon
Subjects:	Q Science > QC Physics > QC173.4.C63 Composite materials
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Ferginia Stany
Date Deposited:	04 Feb 2022 07:42
Last Modified:	04 Feb 2022 07:42
URI:	http://repository.its.ac.id/id/eprint/92785