Pengaruh Arus Pengelasan dan Waktu Penahanan Terhadap Sifat Mekanik Sambungan Las Titik Pada Material Baja SUS301 Dengan DIN 1.4003

Zain, Di Fitra Rezky (2022) Pengaruh Arus Pengelasan dan Waktu Penahanan Terhadap Sifat Mekanik Sambungan Las Titik Pada Material Baja SUS301 Dengan DIN 1.4003. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 02511640000049-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2024. Download (6MB) | Request a copy

Abstract

Di dunia industri terkadang perlu dilakukan penyambungan material-material tak sejenis untuk menurunkan biaya produksi. Oleh karena itu pada penelitian ini bertujuan untuk mendeskripsikan pengaruh parameter variasi arus pengelasan dan waktu penahanan pada las titik terhadap kekuatan tarik dan nilai kekerasan pada sambungan las dua material berbeda dengan variasi tersebut serta mencari parameter las yang memiliki hasil terbaik dalam pengujian kekuatan tarik maupun kekerasan sambungan las. Penelitian ini menggunakan bahan material baja tahan karat austenitic tipe SUS301 dan baja tahan karat ferritic tipe DIN 1.4003 dengan tebal masing-masing 1.5 mm dan 2.0 mm. Proses ini menggunakan portable spot welding machine dengan variasi parameter arus yaitu 8, 8.5, dan 9 kA. Sedangkan variasi waktu penahanan adalah 1.2, 1.4, dan 1.6 detik. Pengujian yang dilakukan untuk menentukan sifat mekanik sambungan las titik yaitu pengujian tarik dan pengujian kekerasan Vickers dari hasil lasan. Variasi terbaik dari hasil lasan terdapat pada arus listrik 9 kA dengan waktu pengelasan 0.4 detik dan waktu penahanan 1.2 detik dengan kekuatan tarik sebesar 381.35 MPa dan memberikan kekerasan terbesar terdapat pada weld nugget dengan nilai sebesar 484 VHN.
================================================================================================
In the industrial factory, it is sometimes necessary to connect dissimilar materials to reduce production costs. Therefore, this study aims to describe the effect of the parameter variations in welding current and holding time on spot welding on the tensile strength and hardness values of welded joints of two different materials with these variations and to find the welding parameters that have the best results in testing the tensile strength and hardness of the joint weld. This research uses austenitic stainless steel type SUS301 and ferritic stainless steel type DIN 1.4003 with a thickness of 1.5 mm and 2.0 mm, respectively. This process uses a portable spot welding machine with variations in current parameters, namely 8, 8.5, and 9 kA. While the variation of holding time is 1.2, 1.4, and 1.6 seconds. Tests carried out to determine the mechanical properties of point welded joints are tensile testing and Vickers hardness testing of the welds. This test uses the test standard, namely AWS D8.9-97. The best variation of the weld results is an electric current of 9 kA with a welding time of 0.4 seconds and a holding time of 1.2 seconds with a tensile strength of 381.35 MPa and provides the greatest strength in the weld nugget with a value of 484 VHN.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	DIN 1.4003, Mechanical properties, Sifat mekanik, Spot welding, SUS301
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.42 Hardness properties and tests. Hardness--Testing. T Technology > TA Engineering (General). Civil engineering (General) > TA492.W4 Welded joints T Technology > TS Manufactures > TS227 Welding.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Di Fitra Rezky Zain
Date Deposited:	10 Feb 2022 02:14
Last Modified:	10 Feb 2022 02:14
URI:	http://repository.its.ac.id/id/eprint/93451