Fikri, Muhammad Aulia (2022) Pembuatan Dan Karakterisasi Dasar Sifat Mekanis Paving Block Menggunakan Campuran Sampah Plastik Sebagai Substitusi Agregat. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02111740000111-Undergraduate_Thesis.pdf - Accepted Version Download (3MB) | Preview |
Preview |
Text
02111740000111-Undergraduate_Thesis.pdf Download (3MB) | Preview |
Abstract
Di Indonesia atau lebih spesifiknya di daerah Balung Kulon, Jember sudah dilakukan proses penyortiran sampah plastik. Penyortiran ini dilakukan oleh lembaga BUMDES Karya Mandiri Balung Kulon dengan menggunakan metode sink-float. Pada proses ini, sampah plastik dibagi menjadi dua tipe, yaitu plastik mengambang dan juga plastik tenggelam. Plastik yang mengambang saat dilakukan penyortiran dikumpulkan lalu dikirim ke pabrik. Sedangkan untuk plastik yang tenggelam tidak dikirim ke pabrik dan dibuang atau tidak digunakan. Perbandingan antara plastik mengambang dan juga plastik tenggelam dari keseluruhan sampah plastik yang diproses atau disortir sebesar 80% untuk plastik mengambang, dan 20% untuk plastik tenggelam. Oleh karena itu, diperlukan suatu tindakan yaitu dengan mendaur ulang sampah plastik tenggelam sehingga tidak mencemari lingkungan kembali. Salah satu tindakan yang mungkin dilakukan addalah menggunakan sampah plastik tenggelam atau sebesar 20% dari keseluruhan sampah yang terkumpul di BUMDES Karya Mandiri Balung Kulon menjadi sebuah barang yang berguna seperti paving block.
Penelitian yang dilakukan menargetkan aplikasi komposit semen sebagai material pembuatan paving block. Seperti yang sudah disebutkan sebelumnya, sampah plastik digunakan sebagai pengganti agregat. Persentase plastik yang digunakan sebesar 10%, 20%, dan 30% dari berat agregat kasar yang digunakan. Komposisi ini pernah diaplikasikan sebelumnya dalam penelitian yang berjudul Experimental Investigation on Paver Blocks with Partial Replacement of Coarse Aggregates with Plastic Waste yang dibuat oleh C. Balaji, dkk. Pada penelitian ini didapat hasil uji tekan yang beragam dari masing – masing komposisi splastik yang digunakan.
Pada penelitian kali ini, digunakan variasi massa pada sampah plastik cacah sebesar 10%, 20%, dan 30% sebagai pengganti pasir halus dalam pembuatan paving block. Didapatkan Nilai massa jenis rata –rata tertinggi dari paving block 0 yaitu 2.212 g/cm3. Sedangkan nilai massa jenis rata – rata terendah didapat dari paving block 30 dengan penggunaan 30% dalam pencampurannya sebagai pengganti pasir halus, yaitu sebesar 1.715 g/cm3. Sedangkan untuk pengujian tekan, didapat nilai kekuatan tekan rata – rata tertinggi yaitu pada paving block 0 yaitu 18.886 MPa. Sedangkan nilai kekuatan tekan terendah didapat dari paving block 30 dengan penggunaan 30% dalam pencampurannya sebagai pengganti pasir halus, yaitu sebesar 8.070 MPa.
================================================================================================
In Indonesia or specifically in Balung Kulon, Jember waste plastic grouping or sortation has been done. This sorting process has been done by an institution name BUMDES Karya Mandiri Balung using sink – float method. In this process, waste plastic divided into two groups, such as the floating waste plastic, and the sinking waste plastic. Waste plastic that floats after the sorting process, be gathered and sent to the recycling industry. Meanwhile, the sinking waste plastic cannot be used or shipped into the recycling industry and it is thrown away. The ratio between sinking waste plastic and floating waste plastic from the whole plastic that has been collected, processed, and sorted, is 80% for floating waste plastic, and 20% for for sinking waste plastic. That’s why, we need to make an action for recycling the sinking waste plastic that has been collected in BUMDES Karya Mandiri Balung Kulon so it don’t contaminate the environment again. There’s a way to do it. It’s utilizing the sinking waste plastic to make some useful stuff, such as paving block.
The research targeted the application of cement composites as paving block manufacturing materials. As mentioned earlier, plastic waste is used as a substitute for aggregates. The percentage of plastic used is 10%, 20%, and 30% of the aggregate weight used. This composition has been applied previously in research entitled Experimental Investigation on Paver Blocks with Partial Replacement of Coarse Aggregates with Plastic Waste made by C. Balaji, et al. In this study, the results of various compression tests from each of the plastic compositions used.
In this research, used mass variations in chopped plastic waste of 10%, 20%, and 30% as a substitute for fine sand in the manufacture of paving blocks. Obtained the highest average type mass value of paving block 0 is 2,212 g / cm3. While the lowest average density value is obtained from paving block 30 with the use of 30% in mixing it instead of fine sand, which is 1,715 g / cm3. As for compression testing, the highest average compression strength value is obtained on paving block 0 which is 18,886 MPa. While the lowest compressive strength value is obtained from paving block 30 with the use of 30% in mixing it instead of fine sand, which is 8,070 MPa.
| Item Type: | Thesis (Other) |
|---|---|
| Uncontrolled Keywords: | Komposit semen, sampah plastik, paving block, massa jenis, kekuatan tekan, BUMDES Karya Mandiri,Cement composite, plastic waste, density, compression strength |
| Subjects: | T Technology > TE Highway engineering. Roads and pavements > TE251.T74 Pavements--Design and construction |
| Divisions: | Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis |
| Depositing User: | Muhammad Aulia Fikri |
| Date Deposited: | 21 Feb 2022 01:35 |
| Last Modified: | 20 Sep 2024 06:35 |
| URI: | http://repository.its.ac.id/id/eprint/94079 |
Actions (login required)
 |
View Item |