Analisis Kegagalan Thermal Fatigue pada Economizer Tube Heat Recovery Steam Generator

Ulfani, Millenia Firda (2022) Analisis Kegagalan Thermal Fatigue pada Economizer Tube Heat Recovery Steam Generator. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 02111640000071-Undergraduate_Thesis.pdf] Text
02111640000071-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 April 2024.

Download (4MB) | Request a copy

Abstract

Elemen-elemen mesin yang digunakan dalam serangkaian proses produksi, bekerja saling berkaitan satu sama lain. Kerusakan pada salah satu elemen mesin, dengan berjalannya waktu, akan mempengaruhi elemen mesin yang lain sehingga menghambat kerja mesin. Hal ini terjadi pada economizer tube HRSG dimana salah satu tube mengalami kegagalan secara tiba-tiba. Kegagalan tersebut terjadi pada saat proses pemanasan berlangsung. Gagalnya tube menyebabkan kebocoran air pada sistem yang sedang beroperasi sehingga menghambat proses produksi. Oleh sebab itu perlu dilakukan analisis kegagalan dengan beberapa pengujian, diantaranya: pengujian spektrometri, pengamatan makroskopis, dan pengujian metalografi untuk tube yang patah agar tidak terjadi kegagalan yang sama dikemudian hari.
Analisis kegagalan dimulai dengan observasi lapangan untuk mengetahui bentuk dan permukaan patahan tube. Pengambilan data pendukung dilakukan untuk membantu dalam menganalisis kegagalan. Tube dengan bagian yang memiliki permukaan patahan digunakan untuk mengetahui jenis patahannya dan penyebab terjadinya kegagalan. Bentuk dan dimensi tube digunakan untuk melihat adanya antisipasi terhadap perubahan diameter. Pola bagian dalam tube diamati untuk mengetahui korelasinya dengan jenis kerusakan tube.
Pada penelitian ini dapat disimpulkan bahwa, penyebab terjadinya kegagalan material economizer tube HRSG adalah thermal fatigue. Mekanisme terjadinya kegagalan material economizer tube HRSG, yaitu diawali dengan initiation crack pada bagian luar economizer tube, lalu merambat secara melingkar hingga terjadi kegagalan total pada economizer tube. Berdasarkan hasil uji spektrometri dan metalografi, tidak ditemukan tanda-tanda terjadinya overheating.
================================================================================================
Machine elements used in a series of production processes, work in conjunction with each other. Damage to one element of the machine, over time, will affect the other elements of the machine so that it hampers the work of the machine. This happened to the HRSG economizer tube where one of the tubes failed suddenly. The failure occurred during the heating process. The failure of the tube causes water leakage in the operating system, thus hampering the production process. Therefore, it is necessary to do a failure analysis with several tests, including Spectrometry Testing, Macroscopic Observation, and Metallographic Testing for broken tubes so that the same failure does not occur in the future.
Failure analysis begins with field observations to determine the shape and surface of the tube fracture. Supporting data retrieval is carried out to assist in analyzing failures. A tube with a fracture surface is used to determine the type of fracture and the cause of failure. The shape and dimensions of the tube are used to see the anticipation of changes in diameter. The pattern of the inside of the tube was observed to determine the correlation with the type of tube damage.
In this study, it can be concluded that the cause of the failure of the HRSG economizer tube material is thermal fatigue. The mechanism for the failure of the HRSG economizer tube material, which begins with an initiation crack on the outside of the economizer tube, then propagates in a circle until a total failure occurs in the economizer tube. Based on the results of spectrometry and metallographic tests, no signs of overheating were found.

Item Type: Thesis (Other)
Uncontrolled Keywords: economizer tube, HRSG, analisa kegagalan, failure analysis
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA169.5 Failure analysis
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Millenia Firda Ulfani
Date Deposited: 22 Feb 2022 08:11
Last Modified: 14 Apr 2023 04:06
URI: http://repository.its.ac.id/id/eprint/94712

Actions (login required)

View Item View Item