Analisa Sifat Mekanik Beton Geopolimer Dengan Bahan Dasar Fly Ash Dan Larutan Naoh Dengan Molaritas 12 M Dan 14 M Sebagai Aktifator

Permana, Wira Ekha (2008) Analisa Sifat Mekanik Beton Geopolimer Dengan Bahan Dasar Fly Ash Dan Larutan Naoh Dengan Molaritas 12 M Dan 14 M Sebagai Aktifator. Other thesis, Institut Teknologi Sepuluh Nopember Surabaya.

Text 3103100072-Undergraduate_Thesis.pdf - Accepted Version Download (97MB)

Abstract

Saat ini terdapat beton geopolimer yang dapat diusulkan untuk dapat digunakan sebagai altenatif baru selain beton konvensional.Terdapat beberapa hal yang membedakan antara beton geopolimer dan beton konvensional diantaranya yaitu bahan dasar yang digunakan.Beton geopolimer dalam tugas akhir ini menggunakan fly ash sebagai bahan dasar nya.Untuk dapat menghasilkan beton geopolimer dengan kuat tekan yang direncanakan perlu dilakukan penelitian di laboratorium untuk mencari komposisi campuran yang tepat.Molaritas dari aktifator, kandungan air dalam campuran, perawatan (curing ), temperatur pada saat curing dan jenis alkaline yangdigunakan merupakan beberapa faktor yang mempengaruhi perilaku dan kuat tekan beton geopolimer.Dalam pembuatan beton geopolimer ini menggunakan suatu aktivator alkalin sebagai pereaksinya.Aktivator yang digunakan yaitu Sodium Silikat ( Na^SiOj )dan Sodium Hidroksida ( NaOH ). Sodium Hidroksida yang digunakan yaitu Sodium Hidroksida dengan molaritas 12dan 14 M, dan juga menggunakan perbandingan antara Sodium Silikat dan Sodium Hidroksida yang bervariasi yaitu 0,5 ; 1 ; 1,5 ; 2 ; 2,5. Komposisi yang tepat dari bahan - bahan yang ada, proses curing yang tepat dalam proses pembuatan beton geopolimer diharapkan memperoleh beton yang memiliki perilaku mekanis yang memuaskan
========================================================================================================================================
Currently there are geopolymer concretes that can be proposed to be used as a new alternative to conventional concrete. There are several things that distinguish geopolymer concrete from conventional concrete, including the basic materials used. Geopolymer concrete in this final project uses fly ash as its basic material. To be able to produce geopolymer concrete with compressive strength It is planned that laboratory research is needed to find the right mix composition. Molarity of the activator, water content in the mixture, curing temperature, curing temperature and the type of alkaline used are some of the factors that affect the behavior and compressive strength of geopolymer concrete. In the manufacture of geopolymer concrete This uses an alkaline activator as the reactant. The activators used are Sodium Silicate (Na^SiOj) and Sodium Hydroxide (NaOH). The Sodium Hydroxide used is Sodium Hydroxide with molarities of 12 and 14 M, and also uses a comparison between Sodium Silicate and Sodium Hydroxide which varies, namely 0.5; 1 ; 1.5 ; 2 ; 2,5. The right composition of the existing materials, the right curing process in the process of making geopolymer concrete is expected to obtain concrete that has satisfactory mechanical behavior

Item Type:	Thesis (Other)
Additional Information:	RSS 620.136 Per a-1
Uncontrolled Keywords:	Beton geopolimer , Fly ash , molaritas , Sodium
Subjects:	T Technology > TH Building construction > TH1461 Concrete construction.
Divisions:	Faculty of Civil Engineering and Planning > Civil Engineering > 22201-(S1) Undergraduate Thesis
Depositing User:	EKO BUDI RAHARJO
Date Deposited:	14 Dec 2022 07:40
Last Modified:	14 Dec 2022 08:34
URI:	http://repository.its.ac.id/id/eprint/95232

Actions (login required)

View Item