Difraksi Kristal Superkonduktor Ndba2cu307-6, Yba 2cii307-5, Dan ( Ndo,5gdo, 5 Ba 2cu307.Fi )

Hardiyasa, I Made (2010) Difraksi Kristal Superkonduktor Ndba2cu307-6, Yba 2cii307-5, Dan ( Ndo,5gdo, 5 Ba 2cu307.Fi ). Other thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[thumbnail of 1106100055-Undergraduate_Thesis.pdf] Text
1106100055-Undergraduate_Thesis.pdf - Accepted Version

Download (13MB)

Abstract

Telah Dilakukan Penelitian Mengenai Superkonduktor Ndba2cu307^, Yba2cu307^ Dan (Ndo,5gdo,5)Ba2cu307^ Secara Pencampuran Basah Untuk Mengetahui Pola Difraksi Kristal Dengan Menggunakan Sinar-X Dan Neutron. Berdasarkan Hasil Penelitian, Diperoleh Kesimpulan Bahwa Ketiga Superkonduktor Memilki Struktur Ortorombik, Grup Ruang Pmmm No. 47. Fraksi Volume Yang Dihasilkan Untuk Superkonduktor Ndba2cu3(>7^ Adalah 98,53%, Untuk Superkonduktor (Ndo,5gdo,5)Ba2cu307^ Adalah 97,42%Dan Superkonduktor Yba2cu307_S Adalah 99,89%. Teijadi Pengisian Tempat Yang Tidak Penuh Pada Atom Oksigen 02, 03, 04, Dan 05. Penggantian Yttrium(Y) Dengan Neodynium (Nd) Dan Gadolinium (Gd) Mengakibatkan Panjang Ikatan Antar Atom Logam Dengan Oksigen Menjadi Lebih Memanjang. Sedangkan
Untuk Sudut Ikatannya Semakin Mengecil. Jumlah Oksigen Dapat Diketahui Dengan Pengukuran Menggunakan Neutron Untuk Sampel Superkonduktor Ndba2cu307^ Nilai 5 = 0,133 Berarti Jumlah Oksigen Sebesar 6,867 Maka Dapat Ditulis Ndba2cu306,867
======================================================================================================================================
Research has been carried out on the superconductors Ndba2cu307^, Yba2cu307^ and (Ndo,5gdo,5)Ba2cu307^ by wet mixing to determine crystal diffraction patterns using X-rays and neutrons. Based on the research results, it is concluded that the three superconductors have an orthorhombic structure, Pmmm No. Space Group. 47. The resulting volume fraction for superconductor Ndba2cu3(>7^ is 98.53%, for superconductor (Ndo,5gdo,5)Ba2cu307^ is 97.42% and superconductor Yba2cu307_S is 99.89%. Incomplete filling occurs In Oxygen Atoms 02, 03, 04, and 05. Replacement of Yttrium(Y) with Neodynium (Nd) and Gadolinium (Gd) results in the bond length between metal atoms and oxygen becoming longer. For the Bond Angle Getting Smaller. The amount of oxygen can be known by measuring using neutrons for the superconducting sample Ndba2cu307^ Value 5 = 0.133 means that the amount of oxygen is 6.867, so it can be written Ndba2cu306.867

Item Type: Thesis (Other)
Additional Information: RSFi 537.623 Har d
Uncontrolled Keywords: Ndba2cu307s, (Ndo,5gdo,5)Ba2cu307^,Yba2cu307^
Subjects: Q Science > QC Physics > QC611.97.C54 Superconductors
Divisions: Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 29 Dec 2022 06:40
Last Modified: 29 Dec 2022 06:40
URI: http://repository.its.ac.id/id/eprint/95291

Actions (login required)

View Item View Item