Pengaruh Variasi Mol Terhadap Struktur Kristal, Morfologi, Dan Performa Elektrokimia Na2/3fexmnx-1o2 (Nfmo) Sebagai Katoda Sodium Ion Battery (SIB)

Simanjuntak, Dion Refindo (2023) Pengaruh Variasi Mol Terhadap Struktur Kristal, Morfologi, Dan Performa Elektrokimia Na2/3fexmnx-1o2 (Nfmo) Sebagai Katoda Sodium Ion Battery (SIB). Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000012-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2025. Download (2MB) | Request a copy

Abstract

Baterai adalah alat penyimpanan energi bersifat portabel yang sering digunakan dan dikembangkan hingga saat ini.. SodiumIon Battery (SIB) adalah salah satu jenis baterai yang dapat menggantikan baterai ion litium yang paling popular digunakan padaperangkat elektronik portabel. Beberapa kelebihan dari baterai natrium adalah harganya yang lebih terjangkau, ketersediaanyang melimpah, dan memiliki potensi penyimpanan yang tidak jauh berbeda dibanding dengan baterai litium. Pada penelitian ini NaCHCOO ,MnCH3COO, C6H8O7 dan FeNO3 digunakan sebagaiprekursor dalam proses sintesis Na2/3FexMnx -1O2. Dimana penelitian akan menggunakan metode sol-gel serta divariasikan terhadap mol dengan x=0,1; 0,3; dan 0,5 yang akan dikalsinasi pada temperatur 750oC, untuk mengetahui pengaruhnya terhadapmorfologi danperformaelektrokimia dari baterai. Pengujian morfo logi menggunakan X- Ray Difraction (XRD) dan Electrochemical impedance spectroscopy (SEM.). Pengujian performa elektrokimia akan dilakukan melalui pengujian Electrochemical impedance spectroscopy (EIS), Cyclic Voltammetry (CV) dan Gavlanostatic charge-discharge (GCD). Hasil analisis menunjukkan bahwa variasi mol pada katoda NFMO mempengaruhi ukuran kristal yang terbentuk dimana Ukuran kristal terkecil dimiliki oleh NFMO 0.5. hal ini akan menyebabkan katoda NFMO 0.5 akan lebih mudah melakukan transfer ion. Hal ini dibuktikan dengan kapasitas baterai yang dapat ditampung oleh katoda NFMO 0.5 memiliki kapasitas terbesar yaitu, 5,68399 mAh. Hambatan terbesar dimiliki oleh NFMO 0.1 yaitu sebesar 1,137 x 107 ohm, sedangkan hambatan terkecil dimiliki oleh NFMO 0.5 yaitu sebesar 7,174 x 103ohm. Hal ini menyebabkan NFMO 0.5 memiliki kemampuan yang baik dalam menghantarkan listrik, dibuktikan dengan konduktivitas listrik yang dimiliki oleh NFMO 0.5 adalah yang terbesar yaitu 3,48 x 10-2(ohm.cm)-1
=======================================================================================================================================
Batteries are portable energy storage devices that are often used and developed to date. Sodium Ion Battery (SIB) is a type of battery that can replace the most popular lithium ion battery used in portable electronic devices. Some of the advantages of sodium batteries are that they are more affordable, have abundant availability, and have a storage potential that is not much different from lithium batteries. In this study NaCHCOO, MnCH3COO, C6H8O7 and FeNO3 were used as precursors in the Na2/3FexMnx -1O2 synthesis process. Where the research will use the sol-gel method and vary the mole with x = 0.1; 0.3; and 0.5 which will be calcined at a temperature of 750oC, to determine the effect on the morphology and electrochemical performance of the battery. Morphological testing using X-Ray Difraction (XRD) and Electrochemical impedance spectroscopy (SEM.). Electrochemical performance testing will be carried out through Electrochemical impedance spectroscopy (EIS), Cyclic Voltammetry (CV) and Gavlanostatic charge-discharge (GCD) tests. The results of the analysis show that the variation in moles at the NFMO cathode affects the size of the crystals formed where the smallest crystal size is owned by NFMO 0.5. this will cause the NFMO 0.5 cathode to transfer ions more easily. This is evidenced by the capacity of the battery that can be accommodated by the NFMO 0.5 cathode which has the largest capacity, namely 5.68399 mAh. The biggest resistance is NFMO 0.1 which is 1.137 x 107 ohms, while the smallest resistance is NFMO 0.5 which is 7.174 x 103 ohms. This causes NFMO 0.5 to have a good ability to conduct electricity, as evidenced by the electrical conductivity that NFMO 0.5 has is the largest, namely 3.48 x 10-2(ohm.cm)-1

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Sodium Ion Battery, Metode Sol-Gel, variasi mol Sodium Ion Battery, Sol-Gel Method, mole variation
Subjects:	T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL220 Electric vehicles and their batteries, etc.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Dion Refindo Simanjuntak
Date Deposited:	09 Feb 2023 01:58
Last Modified:	09 Feb 2023 01:58
URI:	http://repository.its.ac.id/id/eprint/96539

Actions (login required)

View Item