Komposit Material Dari Pati Jagung - Sodium Acetat Dengan Limbah Industri Fly Ash Sebagai Filler Elektrolit Padat Penghantar Ion Pada Aplikasi Superkapasitor

Erlangga, Irfani Faiq (2023) Komposit Material Dari Pati Jagung - Sodium Acetat Dengan Limbah Industri Fly Ash Sebagai Filler Elektrolit Padat Penghantar Ion Pada Aplikasi Superkapasitor. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5009201088-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2025. Download (3MB) | Request a copy

Abstract

Solid polymer electrolyte (SPE) adalah solusi yang lebih aman dari penggunaan elektrolit cair. Penelitian ini berfokus pada peningkatan konduktivitas ion dari penambahan variasi fly ash pada SPE. Sistesis dibuat dari pati jagung, garam CH3COONa dan fly ash sebagai filler. Penggunaan metode solution casting terbukti berhasil untuk fabrikasi SPE dalam penelitian ini. Berdasarkan pengujian, X-Ray Diffraction (XRD) terjadi perubahan struktur SPE menjadi lebih amorf dibanding tanpa fly ash, adanya interaksi fly ash terlihat adanya sedikit pergeseran gugus fungsi pada gusgus C=OH pada pengujian Fourier Transform Infra-Red (FTIR) , pada hasil SEM juga terlihat interaksi dari fly ash yang menambah ruang dengan lebih banyak gumpalan pada permukaan SPE, fly ash juga menunjukkan kestabilan thermal yang lebih baik pada variasi yang paling tinggi yang ditunjukkan pada hasil Thermo Gravimetric Analysis (TGA). Hasil Electrochemical impedance Spectrometry (EIS) menunjukkan peningkatan konduktivitas ionik pada SPE akibat penambahan fly ash dengan nilai tertinggi pada konsentrasi fly ash 5% sebesar 3,64 x 10-4 S/cm, hal ini menandakan interaksi ion pada polymer yang cukup baik dengan adanya fly ash. Sehingga SPE berbasis pati jagung dengan filler fly ash memiliki potensi untuk digunakan sebagai elektrolit padat pada Superkapasitor.
==============================================================================================================================
Solid polymer electrolyte (SPE) safer solution than used liquid electrolytes. This research focused on increasing the ionic conductivity of the addition of fly ash in SPE. The synthesis made from corn starch, CH3COONa salt and fly ash as filler. The use of the solution casting method proved successful for SPE fabrication in this study. Based on the tests, X-Ray Diffraction (XRD) changes in the SPE structured to become more amorphous than without fly ash, the presence of fly ash interactions shows a slight shift in the functional groups in the C=OH group in Fourier Transform Infra-Red (FTIR) test, results SEM also shows the interaction of fly ash which adds space with more porosity on the SPE surface, fly ash also shows better thermal stability at the highest variation as shown in the results of the Thermo Gravimetric Analysis (TGA). Electrochemical impedance Spectrometry (EIS) results showed a increased ionic conductivity in SPE due to the addition of fly ash with the highest value at a 5% fly ash concentration of 3.64 x 10-4 S/cm, this result indicated a fairly good interaction in the polymer from presence of fly ash. Result from SPE based on corn starch with fly ash filler has been potential to be used as a solid electrolyte in supercapacitors.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Solid Polymer Electrolyte, Ionic Conductivity, Fly Ash
Subjects:	T Technology > TJ Mechanical engineering and machinery > TJ165 Energy storage. T Technology > TP Chemical technology > TP1140 Polymers T Technology > TP Chemical technology > TP255 Electrochemistry, Industrial.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User:	Irfani Faiq Erlangga
Date Deposited:	11 Feb 2023 07:53
Last Modified:	11 Feb 2023 07:53
URI:	http://repository.its.ac.id/id/eprint/96697