Analisis Pengaruh Daya dan Waktu Microwave pada Sintesis AC/CuO sebagai Fotokatalis untuk Konversi CO2 menjadi Methanol

Pandani, Azarine Atha (2023) Analisis Pengaruh Daya dan Waktu Microwave pada Sintesis AC/CuO sebagai Fotokatalis untuk Konversi CO2 menjadi Methanol. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6011201002-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2025. Download (4MB) | Request a copy

Abstract

Semakin pesatnya perkembangan teknologi, semakin besar pula kebutuhan manusia akan energi, yang mengakibatkan semakin meningkatnya gas emisi berupa CO2. CO2 direduksi dengan adanya energi matahari yang mampu mengubah menjadi methanol dengan bantuan fotokatalis. Activated Carbon/CuO dipilih karena tingginya tingkat adsorpsi polutan CO2 pada permukaan katalis serta luas permukaanya yang besar. Penelitian bertujuan untuk menganalisis pengaruh daya dan waktu microwave terhadap struktur, morfologi, dan sifat fotokatalitik AC/CuO. AC/CuO yang digunakan sebagai fotokatalis untuk konversi CO2 menjadi methanol disintesis menggunakan microwave dengan daya 180 W, 300 W, dan 450 W selama 30, 60, dan 90 menit, yang kemudian diuji XRD, FTIR, SEM, UV-Vis, BET, dan GCMS. CuO disintesis dengan menggunakan metode sol-gel untuk kemudian dikompositkan dengan AC menjadi komposit AC/CuO. Semakin besar daya yang digunakan, ukuran kristal komposit AC/CuO juga semakin besar, seiring dengan semakin kecilnya energi band gap yang dihasilkan. Ukuran kristal terbesar dimiliki oleh sampel AC/CuO yang disintesis microwave dengan daya 450 watt selama 90 menit, dengan energi band gap sebesar 3,31 eV, menghasilkan methanol 2,19%, ethanediol 3,26%, dan propanol 15,80%. Sedangkan, komposit AC/CuO yang disintesis dengan daya 180 watt selama 60 menit menghasilkan methanol hasil fotokatalisis terbanyak, yaitu 16,96%.

================================================================================================================================

The more rapid the development of technology, the greater the human need for energy, which results in increasing gas emissions in the form of CO2. CO2 is reduced in the presence of solar energy which can convert it into methanol with the help of a photocatalyst. Activated Carbon/CuO was chosen because of the high adsorption rate of CO2 pollutants on the surface of the catalyst and its large surface area. The aim of this study was to analyze the effect of microwave power and time on the structure, morphology, and photocatalytic properties of AC/CuO. AC/CuO used as a photocatalyst for the conversion of CO2 to methanol was synthesized using a microwave with a power of 180 W, 300 W, and 450 W for 30, 60, and 90 minutes, which were then tested by XRD, FTIR, SEM, UV-Vis, BET, and GCMS. CuO was synthesized using the sol-gel method and then composited with AC to become an AC/CuO composite. The greater the power used, the larger the crystal size of the AC/CuO composite, along with the smaller band gap energy produced. The largest crystal size belongs to the AC/CuO sample which was synthesized in the microwave with 450 watt of power for 90 minutes, with a band gap energy of 3.31 eV, producing 2.19% methanol, 3.26% ethanediol and 15.80% propanol. Meanwhile, the AC/CuO composite synthesized at 180 watts for 60 minutes produced the highest amount of methanol produced by photocatalysis, which is 16.96%.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	AC/CuO, microwave, photocatalyst, CO2 conversion , methanol, fotokatalis, konversi CO2, methanol,
Subjects:	Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 27101-(S2) Master Thesis
Depositing User:	Azarine Atha Pandani
Date Deposited:	13 Feb 2023 00:54
Last Modified:	13 Feb 2023 00:54
URI:	http://repository.its.ac.id/id/eprint/97102

Actions (login required)

View Item