Salsabila, Nisrina Kamilia (2022) Degradasi Fotokatalisis Metilen Biru Dengan Titania Emeraldine. Masters thesis, Institut Teknologi Sepuluh Nopember Surabaya.

Text 6001201016-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 November 2024. Download (4MB) | Request a copy

Abstract

Proses degradasi fotokatalisis merupakan salah satu proses untuk mengurangi pencemaran air yang menarik perhatian banyak peneliti. Proses ini umumnya menggunakan semikonduktor oksida logam sebagai fotokatalis. Semikonduktor oksida logam yang banyak digunakan, yaitu TiO2. TiO2 hanya mampu mengadsorpsi energi foton pada daerah UV, sehingga fotoaktivitasnya terbatas. Pada penelitian ini, komposit PAni/TiO2 (titania emeraldine) telah disintesis dengan metode polimerisasi oksidatif kimia in-situ menggunakan TiO2 hasil sintesis (TiO2(s)) maupun TiO2 komersial (TiO2(k)). Komposit disintesis dengan komposisi variasi rasio molar Anilin (Ani) terhadap TiO2. TiO2 disintesis melalui proses kopresipitasi dengan larutan TiCl3 sebagai prekursor, sedangkan PAni disintesis menerapkan metode polimerisasi oksidatif kimia. Karakterisasi material dilakukan menggunakan XRD, FTIR, SEM, dan UV-Vis spektrofotometer. Hasil uji TiO2(s) dan TiO2(k) menunjukkan bahwa material uji mempunyai fasa anatase. TiO2(s) didapatkan dengan morfologi partikel yang teraglomerasi dibandingkan TiO2(k). PAni yang diperoleh memiliki struktur serat nano. Komposit PAni/TiO2 memperlihatkan struktur partikel TiO2 yang menempel pada jaring/serat PAni. Komposit PAni/TiO2(k) dengan rasio molar ani:titania sebesar 1/10 dapat mempercepat laju degradasi metilen biru diantara sampel yang lain. Hal ini dipengaruhi luas permukaan efektif dan sifat semi-kristalin dari TiO2(s)
======================================================================================================================================
The process of photocatalytic degradation is one of the processes to reduce water pollution that has attracted the attention of many researchers. This process generally uses a metal oxide semiconductor as a photocatalyst. The metal oxide semiconductor that is widely used, namely TiO2. TiO2 is only able to adsorb photon energy in the UV region, so its photoactivity is limited. In this study, the PAni/TiO2 (titania emeraldine) composite was synthesized by in-situ chemical oxidative polymerization method using synthesized TiO2 (TiO2(s)) and commercial TiO2 (TiO2(k)). The composites were synthesized with various compositions of Aniline (Ani) to TiO2 molar ratios. TiO2 was synthesized through coprecipitation process with TiCl3 solution as precursor, while PAni was synthesized using chemical oxidative polymerization method. Material characterization was carried out using XRD, FTIR, SEM, and UV-Vis spectrophotometer. The results of the TiO2(s) and TiO2(k) tests indicated that the test material had anatase phase. TiO2(s) is obtained with agglomerated particle morphology compared to TiO2(k). The PAni obtained has a nanofiber structure. The PAni/TiO2 composite shows the structure of TiO2 particles attached to the PAni mesh/fiber. The PAni/TiO2(k) composite with an ani:titania molar ratio of 1/10 can accelerate the degradation rate of methylene blue among other samples. This is influenced by the effective surface area and semi-crystalline nature of TiO2(s)

Item Type:	Thesis (Masters)
Additional Information:	RTFi 541.395 Sal d-1 2022
Uncontrolled Keywords:	Degradasi, Emeraldine, Fotokatalisis, komposit, PAni, Semikonduktor, Titania; Degradation, Composite, Emeraldine, PAni, Photocatalytic, Semiconductor, Titania
Subjects:	Q Science > QD Chemistry > QD716 Photocatalysis.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45101-(S2) Master Thesis
Depositing User:	EKO BUDI RAHARJO
Date Deposited:	13 Apr 2023 06:02
Last Modified:	13 Apr 2023 06:02
URI:	http://repository.its.ac.id/id/eprint/97863

Actions (login required)

View Item