Fotodegradasi Methylene Blue Dengan TiO2/Resin Dan Sumber Cahaya UV-C

Ningsih, Aprilia Rahayu (2022) Fotodegradasi Methylene Blue Dengan TiO2/Resin Dan Sumber Cahaya UV-C. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111840000033-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until September 2024. Download (3MB)

Abstract

Industri tekstil menghasilkan limbah cair non-biodegradable, salah satunya adalah methylene blue. Senyawa methylene blue mempunyai struktur benzena yang sulit untuk diuraikan, bersifat toksik, karsinogenik dan mutagenik. Pengolahan zat warna sintetis dari limbah industri dapat dilakukan melalui proses fisika (misalnya adsorpsi dan filtrasi), pemurnian kimia (misalnya fotokatalisis dan oksidasi), atau degradasi secara biologis. Fotokatalis merupakan proses dengan menggunakan material semikonduktor dan disinari oleh cahaya dengan energi band gap sama atau lebih besar. Salah satu material semikonduktor adalah TiO2, yang memiliki keuntungan diantaranya: memiliki sifat optik yang baik, tidak beracun, harganya murah, memiliki aktivitas fotokatalis yang baik. Penggunaan TiO2 dalam bentuk serbuk menyebabkan TiO2 terlarut dalam larutan. Resin dapat digunakan sebagai bahan campuran fabrikasi substrat agar TiO2 tidak habis bereaksi dan memudahkan dalam mobilisasi material semikonduktor. Dalam penelitian yang telah dilakukan menggunakan lampu UV-C karena memiliki energi foton yang lebih besar dibanding band gap TiO2. Penataan substrat TiO2/resin secara berlembar akan mengoptimalkan cahaya UV-C untuk menyinari substrat secara merata. Melalui pengujian larutan menggunakan visible spektrofotometer diperoleh penurunan konsentrasi larutan methylene blue selama 22 jam pengujian sebesar 56,47% dari yang semula konsentrasi sebesar 14,5 PPM menjadi 6,3 PPM.
=============================================================================================================================
The textile industry produces non-biodegradable liquid waste, one of which is methylene blue. Methylene blue compound has a benzene structure that is difficult to decompose, is toxic, carcinogenic and mutagenic. Treatment of synthetic dyes from industrial waste can be carried out through physical processes (e.g. adsorption and filtration), chemical purification (e.g. photocatalysis and oxidation), or biological degradation. Photocatalyst is a process using a semiconductor material and irradiated by light with a band gap energy equal to or greater. One of the semiconductor materials is TiO2, which has the following advantages: good optical properties, non-toxicity, low price, good photocatalytic activity. The use of TiO2 in powder form causes TiO2 to dissolve in solution. Resin can be used as a substrate for mixed materials so that TiO2 does not run out of reaction and facilitates the mobilization of semiconductor materials. In research that has been carried out using UV-C lamps because it has a photon energy that is greater than the band gap TiO2. TiO2/resin substrate arrangement in a sheet will optimize UV-C light to illuminate the substrate evenly. Through testing the solution using a visible spectrophotometer, the concentration of methylene blue solution decreased during 22 hours of testing by 56.47% from the original concentration of 14.5 PPM to 6.3 PPM.

Item Type:	Thesis (Other)
Additional Information:	RSFi 541.35 Nin f-1
Uncontrolled Keywords:	Fotokatalis, Methylene Blue, TiO2
Subjects:	Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Mr. Tondo Indra Nyata
Date Deposited:	12 May 2023 07:45
Last Modified:	12 May 2023 07:45
URI:	http://repository.its.ac.id/id/eprint/97917

Actions (login required)

View Item