Perbedaan Sifat Mekanik Hasil Penyambungan Las GTAW Pada Aluminium 6061 Dengan Filler ER4043 Dan ER5356

Sholichuddin, Mochammad (2014) Perbedaan Sifat Mekanik Hasil Penyambungan Las GTAW Pada Aluminium 6061 Dengan Filler ER4043 Dan ER5356. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 2109030088_Non_Degree.pdf Download (1MB)

Abstract

Perkembangan teknologi pengelasan yang berkembang di industri perkapalan saat ini penggunaan las GTAW dengan menggunakan bahan aluminium sebagai bahan pembuatan kerangka kapal dengan metode fillet weld. Penelitian dilakukan dengan menggunakan las GTAW untuk bahan aluminium 6061 MgSi dengan filler ER4043 dan ER5356 pada sambungan V-groove diharapkan dapat mengetahui perbandingan pengelasan dengan filler ER4043 dan filler ER5356. Penelitian tersebut menggunakan 2 spesimen, setelah spesimen dibentuk dan dilas maka dilakukan pengujian tarik, pengujian kekerasan Vickers, serta pengamatan mikrostruktur. Hasil uji kekerasan menunjukkan kekerasan logam berkurang dari logam las ke arah HAZ dan logam induk. Hasil mikrostruktur menunjukkan dari logam induk ke daerah logam las terlihat masing-masing mempunyai bentuk butir cill, columnar dan equiaxial. Sedangkan pengelasan dengan filler ER5356 hasil kekerasan menunjukkan lebih rendah dibandingkan dengan pengelasan dengan filler ER4043. Dari hasil mikrostruktur pada pengelasan dengan filler ER5356 dapat dilihat di daerah logam las permukaan logam las lebih kasar dibandingkan dengan pengelasan dengan filler ER4043.
====================================================================================================================================
Development of welding technology developed in the shipping industry is currently using GTAW welding usingaluminum as materials for ships with the framework of fillet weldmethod. The study was conducted by using the GTAW welding foraluminum 6061 MgSi with ER4043 filler and ER5356 filler on the V-Groove connection is expected to know the comparison welding with ER4043 filler and ER5356 filler. The study used two specimens, after the specimen is formed and welded to the tensile test, Vickers hardness testing and microstructural observations. After conducting measurements, tests, and observations on the specimen material obtained gouging comparison of the with ER4043 filler and ER5356 filler. That the ER5356 welding filler value of have distorted the results of a large and a lower hardness value of the tensile test more lower than 4043 welding filler. The result of the value of hardness at 5356 welding filler is lower than 4043 welding filler

Item Type:	Thesis (Diploma)
Additional Information:	RSM 621.52 Sho p
Uncontrolled Keywords:	Las GTAW, aluminium 6061 MgSi, filler ER4043 dan ER5356, GTAW welding, aluminum 6061 MgSi, filler ER4043 and ER5356
Subjects:	T Technology > TS Manufactures > TS227 Welding.
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3
Depositing User:	Mr. Marsudiyana -
Date Deposited:	25 May 2023 06:58
Last Modified:	07 Jun 2023 07:42
URI:	http://repository.its.ac.id/id/eprint/98001