Analisa Pengaruh Variasi Berat Sekam Padi Pada Matriks Epoksi Resin Terhadap Kekuatan Tarik Serta Morfologinya

Sasmita, Yoga (2019) Analisa Pengaruh Variasi Berat Sekam Padi Pada Matriks Epoksi Resin Terhadap Kekuatan Tarik Serta Morfologinya. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 10211500000123-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Indonesia merupakan negara agraris, yaitu negara yang sebagian besar penduduknya berprofesi sebagai petani. Hal ini didukung dengan kondisi iklim sub-tropis yang dimiliki Indonesia karena berada di daerah ekuator bumi. Salah satu hasil pertanian yang melimpah di Indonesia adalah padi. Pada prosesnya, pertanian padi menghasilkan limbah yang disebut sekam padi. Sekam padi dapat dimanfaatkan sebagai filler pada komposit polimer bermatriks epoksi. Penelitian diawali dengan sekam padi yang ditumbuk, dicacah, dan digiling yang kemudian disaring dengan ukuran 50 mesh. Setelah itu sekam padi dikeringkan dengan cara dioven dengan suhu 1700C selama satu jam untuk mengurangi kadar airnya. Sekam padi yang telah kering dicampur dengan epoksi dengan perbandingan yang telah ditentukan. Campuran tersebut kemudian dicetak pada alumunium foil untuk selanjutnya dioven dengan suhu 1700C selama 1 jam. Spesimen kemudian dipotong dan dihaluskan mengacu pada ukuran ASTM D 638. Setelah itu specimen dilakukan pengujian FTIR, tarik, dan SEM.
Hasil pengujian menunjukkan kekuatan tarik terbesar yaitu pada spesimen 90EP/30SP dengan kekuatan tarik 17,49 MPa. Sementara pada spesimen 80EP/20SP sebesar 17,30 Mpa. Ikatan
kimia yang terbentuk pada kedua spesimen cenderung identik, yaitu terdapat amina, amida, alkana, cincin aromatic dan alcohol. Dari penelitian yang dilakukan, komposit dengan perbandingan
80%EP/20%SP mempunyai struktur morfologi yang lebih baik. Komposit dengan perbandingan 80%EP/20%SP hampir tidak memiliki celah udara, serta mempunyai persebaran epoksi dan sekam padi yang lebih merata.
=================================================================================================================================
Indonesia is an agricultural country, the country that most of the population are farmers. This is supported by a sub-tropical climate conditions that Indonesia because it is located in the equatorial region of the earth. One of the abundant agricultural products in Indonesia is rice. In the process, the rice farming produces waste called rice husk. Rice husk can be used as filler in polymer composites with epoxy. The research begins with ground rice husks, chopped, and milled are then screened with a size of 50 mesh. After the rice husk oven dried at a temperature of 1700C for one hour to reduce the
moisture content. The dried rice husks mixed with epoxy at a predetermined ratio. The mixture is then printed on aluminum foil for subsequent oven with a temperature of 1700C for 1 hour. Specimens are then cut and polished refers to the size of ASTM D 638. After that the specimen is tested with FTIR testing, tensile, and SEM.
The test results showed the greatest tensile strength that is in the specimen 90EP / 30SP with a tensile strength of 17.49 MPa. While the specimen 80EP / 20SP amounted to 17.30 MPa. The chemical bonds formed on both specimens are likely identical, ie there amines, amides, alkanes, aromatic rings and alcohol. From the research conducted, the composite with a ratio of 80% EP / 20% SP has a better morphological structure. Composites with a ratio of 80% EP / 20% SP almost no air gap, as well as having an epoxy dispersion and rice husk are more evenly.

Item Type:	Thesis (Other)
Additional Information:	RSMI 620.118 Sas a-1 2019
Uncontrolled Keywords:	Komposit, Epoksi, Sekam Padi, Fourier Transform Infrared Spectroscopy, Uji Tarik, Scanning Electron Microscopy, Composite, Epoxy, Rice Husk, Fourier Transform Infrared Spectroscopy, Tensile Test, Scanning Electron Microscopy.
Subjects:	H Social Sciences > HD Industries. Land use. Labor > HD9999.C715-.C7154 Composite materials
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering
Depositing User:	- Davi Wah
Date Deposited:	05 Jul 2023 07:43
Last Modified:	05 Jul 2023 07:43
URI:	http://repository.its.ac.id/id/eprint/98314

Actions (login required)

View Item