Desain Alat Uji Efisiensi Anoda Korban Sesuai Standar DNVGL-RPB401 Untuk Paduan Aluminium dengan Variasi Temperatur Elektrolit

Kusuma, Willy Deviet (2023) Desain Alat Uji Efisiensi Anoda Korban Sesuai Standar DNVGL-RPB401 Untuk Paduan Aluminium dengan Variasi Temperatur Elektrolit. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511940000048-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 September 2025. Download (3MB) | Request a copy

Abstract

Korosi merupakan peristiwa penurunan mutu logam yang disebabkan oleh reaksi elektrokimia dengan lingkungan sekitarnya. Korosi bersifat destruktif, berbahaya, dan dapat menyebabkan kerugian yang besar. Korosi tidak dapat dihentikan namun dapat dikendalikan lajunya. Terdapat banyak metode yang dapat digunakan untuk mengendalikan laju korosi, salah satunya adalah dengan proteksi katodik anoda korban. Proteksi katodik anoda korban memanfaatkan prinsip sel galvanik dimana logam yang akan dilindungi atau katoda memiliki potensial yang lebih tinggi dan sebaliknya logam yang akan dikorbankan atau anoda memiliki nilai potensial yang lebih rendah. Salah satu standar praktik yang digunakan untuk mendesain proteksi katodik ini adalah DnVGL-RPB401. Dengan melakukan pengujian sesuai standar DnVGL-RPB401 maka dapat diketahui nilai dari efisiensi anoda korban yang bekerja pada perlindungan katoda. Perlunya mengetahui efisiensi anoda korban adalah untuk mengukur performa dari anoda korban dalam memberikan proteksi pada logam yang akan dilindungi. Penelitian ini dilakukan untuk membuat alat uji efisiensi anoda korban dengan standar DnVGL-RPB401. Pada penelitian ini uji kelayakan menggunakan variasi temperatur elektrolit, yaitu pada temperatur 20°C, 25°C, 30°C, dan 35°C. Hasil efisiensi yang didapatkan untuk temperatur 20°C, 25°C, 30°C, dan 35°C adalah 88.6%, 80.66%, 76.55%, dan 63.23%. Hasil pengujian dari rangkaian yang dirancang ulang mendekati alat uji pada PT. Indocast Fransasia Sejahtera.
==================================================================================================================================
Corrosion is a decrease in metal quality caused by electrochemical reactions with the surrounding environment. Corrosion is destructive, dangerous, and can cause great losses. Corrosion cannot be stopped but its rate can be controlled. There are many methods that can be used to control the rate of corrosion, one of them is the sacrificial anode cathodic protection. Protection of anode cathodic sacrificial utilizes the principle of a galvanic cell where the metal will be protected or the cathode has a higher potential otherwise the metal will be sacrificed or the anode has a lower potential value. One of the standard practices used to design cathodic protection is DnVGL-RPB401. By carrying out tests according to the DnVGL-RPB401 standard, then it can be seen the value of the efficiency of the sacrificial anode working on cathode protection. The efficiency of the sacrificial anode needed to be known to measure the performance of the sacrificial anode in providing protection to the metal to be protected. This research was conducted to make a sacrificial anode efficiency test kit with the DnVGL-RPB401 standard. In this study the feasibility test used electrolyte temperature variations, namely at temperatures of 20°C, 25°C, 30°C, and 35°C. The efficiency results obtained for temperatures of 20°C, 25°C, 30°C and 35°C were 88.6%, 80.66%, 76.55% and 63.23%. The test results of the redesigned circuit approach the test equipment at PT. Indocast Fransasia Sejahtera.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Corrosion, Anode, DNVGL-RPB401, Temperature, Korosi, Anoda, DNVGL-RPB401, Temperatur
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives T Technology > TA Engineering (General). Civil engineering (General) > TA418.75 Corrosion-resistant materials T Technology > TA Engineering (General). Civil engineering (General) > TA462 Metal Corrosion and protection against corrosion T Technology > TA Engineering (General). Civil engineering (General) > TA467 Iron and Steel Corrosion and protection against corrosion
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Willy Deviet Kusuma
Date Deposited:	18 Jul 2023 07:20
Last Modified:	18 Jul 2023 07:20
URI:	http://repository.its.ac.id/id/eprint/98552

Actions (login required)

View Item