Pengaruh Penambahan Al203 Terhadap Sifat Listrik Dan Termal Zn(1-x)AlxO Sebagai Kandidat Material Termoelektrik

Putra, Ilham Ramadhan (2017) Pengaruh Penambahan Al203 Terhadap Sifat Listrik Dan Termal Zn(1-x)AlxO Sebagai Kandidat Material Termoelektrik. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2713100097-Undergraduate_Thesis.pdf - Published Version

Download (4MB) | Preview

Abstract

Material termoelektrik merupakan material yang memiliki kemampuan untuk mengubah energi panas akibat perbedaan temperatur menjadi energi listrik dan sebaliknya. Salah satu jenis material yang menunjukkan sifat termoelektrik adalah material seng oksida (ZnO) yang didoping dengan aluminium (Al). Pada penelitian ini dilakukan proses sintesis material Zn(1-x)AlxO dengan fokus pada variasi komposisi penambahan Al2O3. Material Al2O3 yang digunakan sebagai sumber doping adalah sebesar 0; 1; 2; 3; dan 4 persen atom. Penelitian ini dilakukan dengan metode kopresipitasi. Pengujian yang dilakukan untuk menganalisis sifat listrik dan termal dari material hasil sintesis diantaranya adalah menggunakan X-ray Diffractometer, Scanning Electron Microscopy (SEM-EDX), Differential Scanning Calorimetry-Thermogravimetric Analysis (DSC-TGA), dan LCR meter. Hasil penelitian menunjukkan bahwa nilai konduktivitas listrik secara umum meningkat dengan penambahan jumlah doping dan mencapai hasil maksimum pada nilai doping sebesar 2 persen atom. Sementara, ketahanan termal dari material secara umum stabil dengan peningkatan temperatur hingga 900 derajat Celcius. Material hasil sintesis dapat dijadikan sebagai kandidat material termoelektrik untuk aplikasi pada temperatur tinggi. Kata kunci: termoelektrik, ZnO, Al2O3, doping, kopresipitasi =================================================================== Thermoelectric material is a material that has the ability to convert heat energy due to temperature differences into electrical energy and vice versa. One type of material that shows the nature of the thermoelectric properties is zinc oxide (ZnO) which doped by aluminum (Al). In this research, the synthesis of Zn(1-x)AlxO focused on the variation of Al2O3 addition. Material Al2O3 is used as doping resource with the value of 0; 1; 2; 3; and 4 in atomic percent. This research use the co-precipitation method. The tests were conducted to analyze the electrical and thermal properties used X-ray Diffractometer (XRD), Scanning Electron Microscopy-Energy Dispersive Spectroscopy (SEM-EDX), Differential Scanning Calorimetry-Thermogravimetric Analysis (DSC-TGA), and LCR meter. The results of research obtained that the value of the electrical conductivity generally increases with increasing the number of doping and achieve maximum results in doping value of 2 atomic percent. Meanwhile, the thermal stability properties of the material in general is stable with the increasing of temperature until 900 degrees Celcius. The product can be used as the candidate of thermoelectric materials of applications in high temperatures.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Termoelektrik, ZnO, Al2O3, Doping, Kopresipitasi
Subjects: T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: ILHAM RAMADHAN PUTRA
Date Deposited: 10 Mar 2017 01:50
Last Modified: 05 Mar 2019 04:35
URI: https://repository.its.ac.id/id/eprint/1828

Actions (login required)

View Item View Item