ANALISIS STRUKTUR MIKRO UNTUK MENENTUKAN REMAINING LIFE SUDU TURBIN STAGE KETIGA PADA TURBIN GAS TIPE MW701D

HAKIM, AMRI (2017) ANALISIS STRUKTUR MIKRO UNTUK MENENTUKAN REMAINING LIFE SUDU TURBIN STAGE KETIGA PADA TURBIN GAS TIPE MW701D. Undergraduate thesis, Institut Teknologi Sepuuh Nopember.

[img]
Preview
Text
2112100136-Undergraduate_Theses.pdf - Published Version

Download (4MB) | Preview

Abstract

Sudu turbin adalah bagian turbin yang berfungsi untuk mengkonversi energi kinetik menjadi energi mekanik. Sudu turbin tersebut bekerja pada suhu 750°C dengan putaran hingga 3000 rpm. Oleh karena itu, kegagalan seperti korosi, creep, fatigue dan melepasnya bagian coating sangat mungkin terjadi. Remaining Lifetime Assessment merupakan salah satu cara yang digunakan untuk memperhitungkan sejauh mana mesin-mesin dapat beroperasi secara layak dan memenuhi standar sesuai dengan jangka waktu yang sudah direncanakan. Turbin stage ketiga pada penelitian ini telah dioperasikan selama 99.628 Equivalent Operation Hours (EOH), melebihi dari standar EOH-nya yang hanya 72.000 EOH. Oleh karena itu, perlu diadakan penelitian tentang struktur mikro dari sudu turbin stage ketiga dan pengaruhnya terhadap Remaingin Life. Sampel pada penelitian ini adalah sudu turbin stage ketiga dari turbin gas tipe MW701D, yang terbuat dari material nickel based superalloy. Investigasi awal pada sudu turbin dilakukan secara visual. Selanjutnya dilakukan pemeriksaan struktur mikro (Metallography Test) untuk mengetahui kemungkinan terjadinya kegagalan dan menganalisa sisa umurnya. Pengujian kekerasan (Rockwell Hardness Test) untuk mengetahui kemungkinan terjadinya degradasi nilai kekerasan dari sudu turbin. Dilanjutkan dengan Creep Test Simulation yang hasilnya akan digunakan untuk memperkirakan umur dari sudu turbin tersebut dengan metode Larson-Miller Parameter (LMP). Setelah dilakukan perhitungan terhadap nilai kekerasan maksimal didapatkan nilai remaining life sudu turbin sebesar 44814 hours. Berdasarkan metalografi, diperoleh remaining life sebesar 44534 hours. Hasil simulasi creep dengan menggunakan perangkat lunak SolidWork 2016 didapatkan remaining life sebesar 42013 hours. Sebagai faktor keamanan maka besar remaining life yang disarankan adalah dengan besar terkecil yaitu hasil simulasi creep sebesar 42013 hours. ================================================================= Turbine blade is a part of a gas turbine that serves to convert the kinetic energy into the mechanic energy. The turbine blade operates at temperature of 750°C with rotation up to 3000 rpm. Therefore, a failure such as corrosion, creep, fatique and removed part of the coating is likely occur. Remaining Life Assessment is a method used to calculate the extented time which the machines can operate properly and meet the standards in accordance with the planned period. The third stage turbine blade in this research has been operated for 99.628 Equivalent Operation Hours (EOH), exceed of its standard that only 72.000 EOH. Therefore, there should be research on the microstructure of the third stage turbine blade and its influence on the remaining life. Sample in this research is the third stage turbine blade of the gas turbine MW701D, made of nickel based superalloy material. Initial investigation on this turbine blade is done by visual inspection. Further examination of the micro structure (Metallography Test) is done to determine the failure and analyze the rest of its life. Hardness testing (Rockwell Hardness Test) to determine the degradation of the hardness number of the turbine blade. Followed by Creep Test Simulation that the results will be used to estimate the remaining life of the turbine blade with Larson-Miller Parameter (LMP) method. After calculation of the maximum hardness values obtained that turbine blade’s remaining life is 44.814 hours. Based on metallography test, obtained that the remaining life is 44.534 hours. Creep Simulation results from SolidWork 2016 obtained that the remaining life is 42.013 hours. As a safety factor, the remaining life suggested is the smallest which from creep simulation results for 42.013 hours.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Nickel-based superalloy, Turbine blade, remaining life assessment, micro structure, Larson-Miller Parameter.
Subjects: T Technology > TJ Mechanical engineering and machinery > TJ230 Machine design
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: AMRI HAKIM
Date Deposited: 23 Feb 2017 04:38
Last Modified: 05 Mar 2019 04:19
URI: https://repository.its.ac.id/id/eprint/1860

Actions (login required)

View Item View Item