PENGUKURAN EFISIENSI PANEL SURYA TIPE MONOKRISTALIN DAN KARAKTERISASI STRUKTUR MATERIAL PENYUSUNNYA

SETYANINGRUM, YULI (2017) PENGUKURAN EFISIENSI PANEL SURYA TIPE MONOKRISTALIN DAN KARAKTERISASI STRUKTUR MATERIAL PENYUSUNNYA. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1113100031-Undergraduate_Theses.pdf - Published Version

Download (4MB) | Preview

Abstract

Indonesia merupakan wilayah dengan penyinaran matahari berlangsung sepanjang tahun sehingga cahaya matahari merupakan sumber energi terbarukan yang melimpah yang dapat dikonversikan menjadi energi listrik dengan panel surya. Pada penelitian ini dilakukan pengukuran efisiensi panel surya tipe monokristalin dan karakterisasi material penyusunnya menggunakan uji XRD dan Mikroskopi (Optik dan SEM). Dari hasil uji XRD menunjukkan bahwa material penyusun panel surya yang digunakan adalah Silikon murni. Sementaraitu, hasil pengujian SEM dan microscop optik dapat diketahui bahwa ukuran kristal penyusunnya berukuran 28,6µm x 28,6µm dan tersusun secara rapi serta teratur. Hasil pengukuran menunjukkan bahwa panel surya tipe monokristalin ini menghasilkan efisiensi tinggi ketika suhu permukaan sel surya mendekati suhu kamar karena pada suhu tersebut tegangan output turun dengan arus output naik. Dan efisiensi akan turun saat suhu permukaan sel surya lebih tinggi dari suhu kamar karena pada suhu tersebut tegangan output turun dengan arus output konstan sehingga efisiensi rendah. =================================================================================== Indonesian archipelago has abundant solar radiation over the year, which is a renewable source of energy to be converted into electricity by solar panel. In this research, the efficiency of mono-crystalline solar panel was measured and materials structure was characterized by using XRD and microscope (optical and electron/SEM). The XRD spectrum indicates that material used for solar panels is pure Silicon. Meanwhile, from the result of SEM and optical microscope, it is known that the crystal size of silicon is about 28.6 µm x 28.6 µm showing a good order structure. When the solar panel is at an ambient temperature, the output power is generally high, so that the efficiency is high. However, at higher temperature the output power decreases and the efficiency is lower.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Efisiensi, Intensitas, Mikroskopik, Panel Surya, SEM, XRD, Efficiency, Intensity, Microscopy, Solar Cell,
Subjects: Q Science > Q Science (General)
Q Science > QC Physics
Divisions: Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: YULI SETYANINGRUM
Date Deposited: 25 Jan 2017 04:07
Last Modified: 06 Mar 2019 06:47
URI: https://repository.its.ac.id/id/eprint/3165

Actions (login required)

View Item View Item