Sintesis Komposit Grafena Oksida Terduksi (rGO) Hasil Pembakaran Tempurung Kelapa Tua dengan Seng Oksida (ZnO) Sebagai Superkapasitor

Kurniawan, Arie Fauzi (2016) Sintesis Komposit Grafena Oksida Terduksi (rGO) Hasil Pembakaran Tempurung Kelapa Tua dengan Seng Oksida (ZnO) Sebagai Superkapasitor. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1112100100-Undergraduate-Theses.pdf]
Preview
Text
1112100100-Undergraduate-Theses.pdf - Published Version

Download (1MB) | Preview

Abstract

Sintesis komposit Grafena Oksida Terduksi (rGO) Hasil Pembakaran Kelapa Tua dengan Seng Oksida (ZnO) Sebagai Superkapasitor telah dilakukan. Penelitian ini dilakukan untuk mengetahui nilai kapasitansi dari pembuatan grafena oksida tereduksi (rGO) dengan material ZnO. Penelitian ini dilakukan dengan cara metode komposit antara rGO dengan ZnO, dalam penelitian ini diberikan juga variasi dari komposit ini, yakni berdasarkan komposisi rGO /ZnO (1:1), rGO /ZnO (1:2), rGO /ZnO (2:1). Dalam penelitian ini dilakukan karakterisasi berupa X-Ray Diffractometer (XRD), SEM, dan juga pengukuran kapasitansi menggunakan alat uji berupa Cyclic Voltametri (CV). Dari uji kapasitansi menggunakan CV didapatkan besar kapasitansi pada masing-masing material uji yakni yaitu rGO sebesar 13,42 F/g, ZnO sebesar 2,442188 F/g, rGO-ZnO (1:1) sebesar 2,642188 F/g, rGO-ZnO (1:2) sebesar 7,734375 F/g, rGO-ZnO (2:1) sebesar 7,68125 F/g.

========================================================================================

Synthesis of combining reduced graphene oxide (rGO) from old coconut shell with zinc oxide (ZnO) as supercapacitor has been done. This study was conducted to determine the value of the manufacturing capacity of reduced Graphene oxide (rGO) with ZnO material. The sample was prepared by a variation of the rGO / ZnO (1: 1), (1: 2), and (2: 1 ). Samples were characterized by X-ray diffractometer (XRD), SEM, and also the capacity measurement using test equipment such as Cyclic voltammetry (CV). Resulting capacitance of rGO is 13,42 F/g, ZnO is 2,442188 F/g, rGO-ZnO (1:1) is 2,642188 F/g, rGO-ZnO (1:2) is 7,734375 F/g, rGO-ZnO (2:1) is 7,68125 F/g.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Capacitancy; Kapasitansi; rGO; ZnO.
Subjects: Q Science > QC Physics
Divisions: Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: arie kurniawan
Date Deposited: 11 Apr 2017 04:37
Last Modified: 27 Dec 2018 02:12
URI: http://repository.its.ac.id/id/eprint/3175

Actions (login required)

View Item View Item