Studi Eksperimental Pengaruh Variasi Temperatur Dan Waktu Penahanan Partitioning Pada Proses Quenching – Partitioning Baja JIS S45c Di Atas Temperatur Martensite Start

Hafidh, Muhammad (2017) Studi Eksperimental Pengaruh Variasi Temperatur Dan Waktu Penahanan Partitioning Pada Proses Quenching – Partitioning Baja JIS S45c Di Atas Temperatur Martensite Start. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2111100171-Undergraduate Thesis.pdf]
Preview
Text
2111100171-Undergraduate Thesis.pdf - Published Version

Download (4MB) | Preview

Abstract

Perlakuan panas merupakan salah satu cara untuk
memperbaiki sifat mekanik dari material. Prinsip perlakuan panas
pada baja adalah transformasi fasa austenite menjadi fasa lain.
Proses quenching dan partitioning adalah proses perlakuan panas
untuk memperbanyak jumlah retained austenite pada temperatur
kamar untuk mendapatkan baja hasil perlakuan panas yang kuat,
keras, namun tangguh. Pada penelitian ini akan dilakukan proses
quenching dan partitioning pada baja JIS S45C.
Proses perlakuan panas quenching dan partitioning
dilakukan pada baja JIS S45C dengan pemanasan dalam dapur
sampai temperatur austenisasi 900°C dengan waktu tahan 4 jam.
Proses dilanjutkan dengan pencelupan spesimen dalam salt bath
pada temperatur quenching 230°C dengan waktu tahan 10 detik.
Spesimen yang telah diquenching kemudian dicelupkan dalam salt
bath pada temperatur partitioning yang divariasikan 350°C,
375°C, 400°C dan 425°C dengan variasi waktu tahan 10, 100, dan
1000 detik. Media pendinginan dari temperatur partitioning
adalah air. Spesimen yang telah diberi perlakuan panas akan diuji
untuk mengetahui perubahan yang terjadi pada sifat mekanik dan
struktur mikro. Uji tersebut meliputi uji tarik, uji metalografi dan
uji kekerasan.
Hasil yang didapat dari penelitian ini adalah adanya
peningkatan kekuatan, kekerasan dan ketangguhan dari baja JIS Heat S45C yang diikuti dengan penurunan pertambahan panjang dan reduction area
==================================================================================================================
treatment of steel is one of many ways to improve mechanical properties of materials. The basic principles of heat treatment of steel is to transform austenite phase to other possible form. Quenching partitioning is a heat treatment process to enhance the amount of retained austenite at room temperature condition. This process is aimed to produce a strong, hard but tough steel. JIS S45C steel was used in this experiment.
The experiment begins by heating the steel up to 900 ̊C for 4 hours. The very steel then quenched in water as the media for 10 seconds. Followed by reheating process in salt bath to various temperature from 350°C, 375°C, 400°C and 425°C, and various partitioning time from 10 seconds, 100 seconds to 1000 seconds. The post-partitioning cooling media is water. The next step is to test the treated specimen to see the changes in mechanical properties and microstructure. The tests are tensile test, hardness test, and metallography test.
The results indicates that there are improvements in strength, hardness and toughness of JIS S45C steel followed by decreasing elongation and reduction area due to increased stiffness after the process.
Keywords : JIS S45C steel, quenching and partitioning, retained austenite phase fraction, mechanical properties.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: baja JIS S45C, quenching dan partitioning, fraksi fasa retained austenite, sifat mekanik
Subjects: Q Science > QC Physics > QC271 Temperature measurements
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: - MUHAMMAD HAFIDH
Date Deposited: 13 Apr 2017 03:03
Last Modified: 06 Mar 2019 08:38
URI: http://repository.its.ac.id/id/eprint/3352

Actions (login required)

View Item View Item