Analisis Struktur Grafena Oksida Tereduksi Dari Tempurung Kelapa Tua Dengan Hamburan Sinar-X Sudut Kecil Sinkrotron (SAXS)

Nugraheni, Ananda Yogi (2017) Analisis Struktur Grafena Oksida Tereduksi Dari Tempurung Kelapa Tua Dengan Hamburan Sinar-X Sudut Kecil Sinkrotron (SAXS). Masters thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1115201010-Master-Theses.pdf - Published Version

Download (3MB) | Preview

Abstract

Penelitian berjudul “ Analisis Struktur Grafena Oksida Tereduksi dari Tempurung Kelapa Tua dengan Hamburan Sinar-X Sudut Kecil Sinkrotron (SAXS) “ telah dilakukan dengan memanfaatkan bahan dasar limbah tempurung kelapa tua sebagai bahan pembentukan rGO. Penelitian ini menggunakan metode pencampuran serbuk arang dengan zat asam menggunakan HCL dan proses penyayatan. Variasi yang digunakan adalah perbandingan konsentrasi larutan (0,1M dan 1M) serta waktu penyayatan selama 3 dan 6 jam. Karakterisasi dilakukan dengan menggunakan pengujian XRD, PSA, FTIR dan SAXS. Hasil analisis XRD menunjukkan bahwa terbentuk fasa rGO pada posisi sudut 2θ = 23o dengan bidang (002) dan tereduksinya ukuran partikel pada bidang (100) yang ditandai dengan berkurangnya intensitas puncak pada posisi sudut 2θ = 43o. Hasil analisis PSA menunjukkan bahwa penggunaan proses pencampuran senyawa HCL dalam larutan rGO dari arang tempurung kelapa dapat mereduksi ukuran partikel sehingga muncul beberapa puncak di daerah kurang dari 10, 100 nm dan lebih dari 1μ. Hasil analisis FTIR menunjukkan bahwa telah tersisipnya atom - atom Cl pada ikatan antar lapisan rGO sehingga dapat mereduksi ukruan partikel, yang ditandai dengan munculnya puncak untuk ikatan C-Cl pada bilangan gelombang sekitar 423cm-1. Hasil analisis SAXS menggunakan model Guinier dan BeaucageExPoLaw menunjukkan bahwa partikel dalam larutan memiliki radius dibawah 10 nm dengan radius yang beragam karena dispersitas yang rendah serta hasil pencocokan menunjukkan bentuk partikel secara garis besar berbentuk bongkahan bola kasar. Hamburan x-ray yang dihasilkan memiliki intensitas yang sangat rendah disebabkan oleh konsentrasi partikel dalam larutan yang rendah. ====================================================================================== Structural Analysis of Reduced Graphene Oxide (rGO) from Old Coconut Shell by Small Angle X-Ray Scattering (SAXS) has been carried out by utilizing coconut shell. The purpose of this work is to obtain the thickness layer of rGO by using mixing method between charchoal powder with HCL in different molarity and exfoliation time variation. Molarity variation that used were 0,1M and 1M also exfoliation time for 3 and 6 hours. Characterization was performed using XRD, PSA, FTIR and SAXS. XRD analysis shows that the reduced graphene oxide phase is formed with broad peak at 2θ = 23o at (002) and low intensity peak at 2θ = 43o due to the decreasing of particle size at (100) plane. PSA analysis shows that mixing method using HCL and exfoliation process in solution has reduced the thickness layer of rGO which appear at some peaks below 10 and 100 nm also more than 1μ. FTIR result shows that Cl atom has been substituted on Van der Waals bond between layer that cause reduction thickness of rGO which marked by the appearance of C-Cl bond peak at 423cm-1. SAXS analysis using Guinier and BeaucageExPolaw model shows that particles in solution consist of particle with radii below 10 nm and consist of various sizes that are not homogeneous. Fitting curve shows that the form factor of particles are spherical particles with mass fractal. Small particles seen in high q range which were aggregate to form the big particles that appear in low q range. X-ray scattering of the sample has a very low intensity due to the low concentration of particle in solution.

Item Type: Thesis (Masters)
Uncontrolled Keywords: grafena oksida tereduksi (rGO); ukuran partikel; thickness of rGO; SAXS; reduced graphene oxide (rGO); particle size
Subjects: Q Science > QC Physics
Divisions: Faculty of Mathematics and Science > Physics > 45101-(S2) Master Thesis
Depositing User: ANANDA YOGI NUGRAHENI
Date Deposited: 17 Apr 2017 01:55
Last Modified: 08 Mar 2019 06:45
URI: https://repository.its.ac.id/id/eprint/3679

Actions (login required)

View Item View Item