Pengaruh Konsentrasi TiO2 Pada Aplikasi Fotokatalisis Dalam Penjernihan Air Dengan Menggunakan Cat Sebagai Media Perekat

Nurjannah, Anisa (2017) Pengaruh Konsentrasi TiO2 Pada Aplikasi Fotokatalisis Dalam Penjernihan Air Dengan Menggunakan Cat Sebagai Media Perekat. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
2412100020-Undergraduate-Theses.pdf
Restricted to Repository staff only

Download (1MB) | Request a copy

Abstract

Telah dilakukan penelitian tentang pengaruh penambahan TiO2 pada aplikasi proses fotokatalisis dengan media perekat cat besi sebagai upaya proses penjernihan air. TiO2 struktur anatase dan komersil dilarutkan dalam cat besi dengan perbandingan komposisi TiO2 0,5; 1; 1,5; 2; 2,5 gram dengan massa cat tetap yaitu 20 gram. Selanjutnya cat yang telah dicampur dengan TiO2 dilapiskan pada stik es krim. Stik yang telah dilapisi TiO2 dimasukkan ke dalam 100 ml air yang sudah diberi zat pewarna merah, kemudian diberi perlakuan penyinaran dengan sinar matahari 6 jam/hari selama 8 hari. Hasil pengamatan dan uji absorbansi menunjukkan bahwa semakin besar konsentrasi TiO2 semakin besar kecenderungan (trend) penurunan nilai absorbansinya. Penurunan nilai absorbansi terbesar diperoleh sebesar 62,84% yakni dari sampel air yang diberi stik dengan lapisan TiO2 komersil 2,5 gram. Adapun hasil pengujian bakteri menunjukkan bahwa TiO2 dapat menekan pertumbuhan bakteri sebesar 78,48%. ===================================================================================== Has been done this research on the effect additional TiO2 on the application process photocatalytic to an adhesive media paint as the process of water purification. TiO2 anatase structure and commercial dissolved in paint by comparison composition TiO2 0,5; 1; 1,5; 2; 2,5 grams to the mass paint fixed 20 grams. Next, paint has been mixed with TiO2 superimposed in stick ice cream. Stick ice cream in the sample dipped in water volume 100 ml who had been dyes red. Done the measurement of absorbance everyday after sun-dried for six hours at 08.00-14.00 within 8 days. The result of the observation and absorbance measurement shows that the higher concentration TiO2 the less absorbance value. In addition, the testing bacteria shows that TiO2 reduce baccterial growth of 78,48%.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: penjernihan air; fotokatalisis; konsentrasi TiO2; water purification; photocatalytic; TiO2 concentration; stick ice cream
Subjects: H Social Sciences > HD Industries. Land use. Labor > HD4465 Water utilities--Rates
Q Science > QC Physics
Divisions: Faculty of Industrial Technology > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User: Mrs Anis Wulandari
Date Deposited: 04 May 2017 08:05
Last Modified: 22 Dec 2017 07:55
URI: https://repository.its.ac.id/id/eprint/41214

Actions (login required)

View Item View Item