Amobilisasi Ion Logam Cr3+ Dari Limbah Pelapisan Logam Menggunakan Geopolimer Yang Disiapkan Dengan Metode Pencampuran Bertahap

Rosyidah, Maslihatur (2017) Amobilisasi Ion Logam Cr3+ Dari Limbah Pelapisan Logam Menggunakan Geopolimer Yang Disiapkan Dengan Metode Pencampuran Bertahap. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1412100081-Undergraduate Thesis.pdf] Text
1412100081-Undergraduate Thesis.pdf - Published Version
Restricted to Repository staff only

Download (1MB) | Request a copy

Abstract

Geopolimer berbasis abu layang PT IPMOMI berhasil disiapkan menggunakan metode pencampuran reaktan secara bertahap. Geopolimer disiapkan dari abu layang dengan ukuran berbeda – beda, yakni abu layang yang lolos ayakan 60 mesh (FA 60), 100 mesh (FA 100), dan 200 mesh (FA 200). Hasil uji kuat tekan geopolimer menunjukkan abu layang dengan ukuran partikel 100 (FA 100) memiliki kuat tekan tertinggi sebesar 33,59 MPa. Amobilisasi logam berat Cr3+ dilakukan pada geopolimer dengan kuat tekan tertinggi (FA 100). Ion logam berat Cr3+ berasal dari limbah industri pelapisan logam dan limbah buatan dari senyawa Cr(NO3)3∙9H2O. Kuat tekan geopolimer dengan kontaminan Cr3+ dari limbah pelapisan logam dan limbah buatan lebih rendah daripada geopolimer blanko yakni masing – masing sebesar 26,42 MPa, dan 24,47 MPa. Uji leaching menunjukkan tidak ada ion logam Cr3+ yang ter-leaching untuk kedua jenis logam yang menunjukkan bahwa geopolimer mampu mengamobilisasi ion logam Cr3+ dengan baik.
============================================================================================
Geopolymer based on PT. IPMOMI fly ash was succesfully prepared using steps reactan mixing methode successfully. Geopolymer was prepared from fly ash with various of particel sixe, that was fly ash which passed sieve 60 mesh (FA 60), 100 mesh (FA 100), and 200 mesh (FA 200). The result of geopolymer compressive strength showed that FA 100 possesed the highest compressive strength, 33,59 MPa. Immobilization of heavy metal Cr3+ used geopolymer was done to the geopolymer possesing highest compressive strength (FA 100). The source of heavy metal ion Cr3+ are from electroplating industry waste and artificial waste from made of Cr(NO3)3∙9H2O. The compressive strength value of geopolymer which contain Cr3+ contaminant from electroplating waste and artificial waste are lower than blanko geopolymer, which are 26,42 and 24,47 MPa respectively. Leaching test showed no metal Cr that leached for both waste which showed that geopolymer can immobilize metal ion Cr3+ well.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 541.225 Ros a
Uncontrolled Keywords: geopolimer, amobilisasi, limbah Cr3+, abu layang.
Subjects: Q Science > QD Chemistry
Q Science > QD Chemistry > Polymerization
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 02 Jun 2017 03:33
Last Modified: 18 Dec 2017 02:14
URI: http://repository.its.ac.id/id/eprint/41457

Actions (login required)

View Item View Item