Evaluasi Korosi Pada Bagian Luar Tube HRSG Dan Metode Pencegahannya (Studi Kasus PLTGU PT.PJB UP Gresik)

Putra, Bagus Adi Mulya (2016) Evaluasi Korosi Pada Bagian Luar Tube HRSG Dan Metode Pencegahannya (Studi Kasus PLTGU PT.PJB UP Gresik). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2113105023-Undergraduate-Thesis.pdf - Published Version

Download (2MB) | Preview

Abstract

Heat Recovery Steam Generator (HRSG) merupakan suatu alat yang berfungsi menaikkan efisiensi turbin gas pada pembangkit listrik. PT PJB unit Gresik memiliki beberapa HRSG yang sering mengalami korosi pada pipanya. Penelitian ini membahas korosi pada permukaan luar pipa untuk mencari penyebab dan cara pencegahannya. Dalam penelitian ini digunakan metode Root Cause Failure Analysis (RCFA) untuk menentukan penyebab kerusakan akibat korosi. Data yang digunakan adalah pola operasi HRSG, bahan bakar, emisi gas buang, treatment pada HRSG dan analisa sampel sisi luar tube yang terkorosi. Siklus mati hidup HRSG yang sangat tergantung pada kebutuhan daya listrik masyarakat merupakan penyebab utama korosi. Saat HRSG dimatikan dalam waktu yang lama, korosi terjadi pada permukaan fin tube HRSG oleh acid dew point karena sulfur yang terkandung bahan bakar turbin gas. Disarankan untuk melakukan preservasi menggunakan dehumidifikasi untuk menurunkan kelembaban agar kerusakan akibat korosi bisa dihindari. ================================================================================================================== Heat Recovery Steam Generator (HRSG) is an equipment to increase efficiency of gas turbine in power plant. PT.PJB GRESIK has some HRSG which have severe corrosion at outer surface its tube. This research focus in finding the cause of the problem and how to prevent it. Root Cause Failure Analysis (RCFA) methode is used to find cause and damage result by corrosion. The RCFA methode that used are observe operation pattern of HRSG, type of fuel consumed, exhaust gas emission, prevention treatment of HRSG and XRD analysis of the corroded Pre-heater tube sample. On-off cycle of the HRSG, that depend on power demand, is the main cause corrosion. When HRSG was off for a long period of time, corrosion could attack fin tube surface due to acid dewpoint. Sulfur is from the gas turbine fuels. It was sugested that preservaton with dehumidifier should be done to reduce moisture to prevent the corrosion in HRSG chamber.

Item Type: Thesis (Undergraduate)
Additional Information: RSM 620.112 23 Put e
Uncontrolled Keywords: HRSG, korosi tube, RCFA, Dehumidifikasi
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Users 13 not found.
Date Deposited: 22 Jun 2017 06:36
Last Modified: 27 Dec 2018 04:23
URI: https://repository.its.ac.id/id/eprint/41823

Actions (login required)

View Item View Item