Sintesis Serbuk Nano-Zirkon Dengan Metode Penggilingan Dan Anil

Lestari, Novia Dwi (2017) Sintesis Serbuk Nano-Zirkon Dengan Metode Penggilingan Dan Anil. Undergraduate thesis, Insitut Teknologi Sepuluh Nopember.

[thumbnail of 1113100023-Undergraduate_Theses.pdf]
Preview
Text
1113100023-Undergraduate_Theses.pdf - Published Version

Download (964kB) | Preview

Abstract

Penelitan ini bertujuan untuk mengetahui pengaruh penggilingan dan anil terhadap perubahan ukuran kristal dan regangan serbuk zirkon. Bahan dasar yang digunakan yaitu serbuk hasil pemurnian pasir zirkon alam dari Kereng Pangi, Kalimantan Tengah. Serbuk zirkon hasil ekstraksi digiling dengan variasi waktu penggilingan 5, 10, 20 dan 30 jam. Setiap tahap penggilingan dilanjutkan dengan anil selama 2 jam dengan temperatur 200 ○C. Karakterisasi terhadap fasa dilakukan dengan menggunakan uji X-Ray Diffraction (XRD) terhadap fasa sesudah penggilingan serta sesudah anil. Identifaksi fasa dilakukan menggunakan perangkat lunak Match2! dan analisis komposisi fasa menggunakan perangkat lunak Rietica. Selanjutnya dilakukan juga analisis menggunakan perangkat lunak MAUD untuk mengetahui ukuran kristal dan regangan. Hasil analisis menunjukkan bahwa (1) fasa-fasa teridentifikasi adalah zirkon untuk sampel Z0, ZM1,ZM2 dan ZM, (2) zirkon dan zirkonia untuk sampel ZM4, ZMA4, ZM6 dan ZMA6, (3) ukuran kristal zirkon turun dari 162 nm untuk sampel Z0 menjadi 37 nm dari sampel ZM6 . Sebagai tambahan, pada penelitian juga dilakukan pengamatan menggunakan Scanning Electron Microscope (SEM) dan Tranmmison Electron Microscopy (TEM).

================================================================

The objective of this research is to observe the effect milling and annealing on crystallite size and strain of zircon. The basic material was purifed zircon sand from Kareng Pangi, Kalimantan Tengah. The milling was varied for 5, 10, 20,and 30 hours where annealing was done at 200 ○C for 2 hours for each milling step. The phase characterization was done by analyzing the X-ray Diffraction (XRD) data, i.e. using Match2! for phase identification, Rietica for phase composition and MAUD for crystallite size and strain determination. Results showed that (1) the identified phases were zircon for the Z0, ZM1, ZMA1, ZM2, ZMA2 sampel’s, (2) the phase compoisitions were zircon and zirconia for the ZM4, ZMA4, ZM6 and ZMA6, (3) the crystallite size reduced by milling and achieving nanometric orde at 173 for the Z0 to 37 nm for the ZM6. In this research, the observation is also done using Scanning Electron Microscope (SEM) dan Tranmmison Electron Microscopy (TEM).

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: pasir zirkon, penggilingan, zircon sand, milling
Subjects: Q Science
Q Science > QC Physics
Divisions: Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: NOVIA DWI LESTARI
Date Deposited: 18 Sep 2017 02:17
Last Modified: 05 Mar 2019 04:32
URI: http://repository.its.ac.id/id/eprint/42876

Actions (login required)

View Item View Item