Analisis Balistik Impak Peluru Frangible dengan Metode Smoothed Particle Hydrodynamics (SPH)

Simaremare, Peniel Andika Yohannes (2017) Analisis Balistik Impak Peluru Frangible dengan Metode Smoothed Particle Hydrodynamics (SPH). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
2713100095-Undergraduate_Theses.pdf - Accepted Version
Restricted to Repository staff only

Download (4MB) | Request a copy

Abstract

Peluru konvensional terbuat dari bahan timbal yang menimbulkan beberapa kekurangan seperti efek peluru nyasar (richochet), peluru mengenai penembak sendiri (backsplash), dan kerugian kesehatan akibat paparan ledakan timbal di udara. Sedangkan peluru frangible, selain terbuat dari komposit antara Cu-Sn yang ramah lingkungan, juga bersifat mudah terhambur menjadi fragmen-fragmen kecil ketika bertumbukan dengan sasaran tembak. Untuk mengetahui pola hamburan dari peluru frangible digunakan bentuk pemodelan ABAQUS CAE_STUDENT_VER. dengan metode analisa numerik smoothed particle hydrodinamics (SPH). Penelitian sebelumnya yang dilakukan Firmansyah (2015), mengevaluasi Frangibility Factor dari suatu peluru dengan perlakuan temperatur sintering yang divariasikan (200,300,400,500,600 oC). Modulus elastisitas yang dihasilkan adalah 54383,9 ; 57276,86 ; 61270,76 ; 67157,48 ; 76597,16 MPa. Penelitian ini dilakukan untuk menganalisa secara numerik kekuatan impak yang terjadi ketika benturan menggunakan metode elemen hingga berdasarkan penelitiannya Firmansyah. Parameter proses yang digunakan adalah modulus elastisitas hasil proses sintering. Parameter respon yang diharapkan adalah kekuatan impak, frangibility factor, dan ukuran fragmen yang terbentuk. Hasil yang didapat adalah 39,57; 54,87 ; 86,43 ; 157,41 ; 358,41 J untuk energi batas kinetik dimana errornya berdasarkan hasil perhitungan analitis adalah 0,02 ; 0,03 ; 0,17 ; 2,21 ; dan 2,39 dalam persen. Nilai dari frangibility factor adalah 9,02 ; 6,16 ; 3,76 ; 2,09 ; 1,01 dimana errornya berdasarkan hasil perhitungan analitis adalah 2,10 ; 7,36 ; 10,90 ; 7,52 ; dan 5,76 dalam persen. ======================================================================== Conventional bullets made from lead have some shortages such as richochet, backsplash, and the air exposure of lead that can damaging our healthy. Meanwhile, the frangible bullet that made from composites of powder metallurgy between Cu-Sn which is environmentally friendly it also can be deformated into small particles after hit the target. The ABAQUS CAE_STUDENT_VER can help us to assuming and also give the modelling simulation of this whole process. Solid particle hydrodynamics is used to execute the fragmented paricles of frangible bullet. The SPH is meshless methode which is give some advantages to show the scattering of the bullet, because there is no mesh bonding.. Previous research conducted by Firmansyah (2015), to evaluate Frangibility Factor from a bullet which sintered in varied temperature (200,300,400,500,600 oC). Modulus of elasticity produced is 54383.9; 57276.86; 61270.76; 67157.48; 76597.16 MPa. This study was conducted to analyze numerically impact strength that occurs when the collision using finite element method based on research Firmansyah. The process parameters used are modulus of elasticity from sintering process. Respons parameter is impact strength and size of fragments which formed. The result is 39,57; 54,87 ; 86,43 ; 157,41 ; 358,41 J for kinetic energy limit where the error based on result of analytical calculations is 0,02 ; 0,03 ; 0,17 ; 2,21 ; and 2,39 in percent. And the frangibility factor is about 9,02 ; 6,16 ; 3,76 ; 2,09 ; and 1,01 where the error based on result of analytical calculations is 2,10 ; 7,36 ; 10,90 ; 7,52 ; dan 5,76 in percent.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: frangible, peluru, balistik, Cu-Sn10% wt, hamburan, smoothed particle hydrodynamics
Subjects: Q Science > QA Mathematics > QA76 Computer software
T Technology > TA Engineering (General). Civil engineering (General) > TA347 Finite Element Method
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Peniel Andika Yohannes Simaremare
Date Deposited: 12 Sep 2017 03:43
Last Modified: 21 Nov 2020 11:11
URI: https://repository.its.ac.id/id/eprint/43650

Actions (login required)

View Item View Item