Penyisipan Ion Na Pada Gugus Grafena Oksidasi Tereduksi Dari Hasil Pembakaran Tempurung Kelapa Dan Karakterisasinya

Puspitasari, Niken Sylvia (2017) Penyisipan Ion Na Pada Gugus Grafena Oksidasi Tereduksi Dari Hasil Pembakaran Tempurung Kelapa Dan Karakterisasinya. Masters thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1115201003-Master-Theses.pdf]
Preview
Text
1115201003-Master-Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Penelitian tentang “Penyisipan Ion Na Pada Gugus Grafena Oksidasi Tereduksi dari Hasil Pembakaran Tempurung Kelapa dan Karakterisasinya”, telah dilakukan dengan memanfaatkan bahan dasar tempurung kelapa. Penelitian ini bertujuan untuk mengetahui pengaruh dari penyisipan ion Na pada rGO terhadap fasa dan sifat kemagnetan yang muncul. Serbuk arang tempurung kelapa hasil karbonisasi dilarutkan ke dalam aquades dengan menambahkan rGO dan NaCl dengan perbandingan konsentrasi 1:1, 1:2, 2:1. Prosedur yang sama dilakukan pada campuran rGO dan NaOH. Karakterisasi dilakukan dengan menggunakan XRD, FTIR, SEM, EDX dan SQUID. Dari hasil analisis XRD sampel yang telah disisipi Na yang berasal dari NaCl membentuk fasa NaCl walaupun fasa rGO tetap ada, sedangkan sampel yang dicampur NaOH terdapat fasa rGO. Dari hasil analisis FTIR sampel rGO dan rGO:NaCl 1:2 mengandung ikatan C=C, , sedangkan rGO:NaOH 1:2 mengandung ikatan C-NO2. Hasil XRD diperkuat dengan analisis morfologi dengan uji SEM dan komposisi unsur dengan uji EDX. Berdasarkan analisis uji SQUID dengan adanya berbagai variasi konsentrasi Na terhadap rGO, berpengaruh terhadap kemagnetannya dan nilai kemagnetan meningkat dengan penambahan impuritas Na dengan konsentrasi lebih tinggi dari pada rGO (M ~0,03 emu/g) dikarenakan unsur Na yang sedikit mengisi kekosongan unsur yang hilang pada kisi honeycomb rGO yang berikatan kovalen tunggal maupun rangkap dengan unsur C.

=================================================================

“The insertion of Na ions in the reduced graphene oxide from burning coconut shell and its characterization”, has been carried by utilizing coconut shell base material. The purpose of this work to determine effect the insertation of Na ions in rGO for the phase and magnetism properties that appear. Coconut shell charcoal produced by carbonization was dissolved into aquades by adding rGO and NaCl concentration with a ratio of 1: 1, 1: 2, 2: 1. The same procedure is performed on a mixture of rGO and NaOH. Characterization have been used XRD, FTIR, SEM, EDX and SQUID. The same procedure is performed on a mixture of rGO and NaOH. Characterization is done using XRD, FTIR, SEM, EDX and SQUID. From the result of XRD analysis the sample Na inserted from NaCl form NaCl phase even though rGO phase still exist, whereas NaOH mixed samples have rGO phase. From the results of FTIR analysis of rGO and rGO samples: NaCl 1: 2 contains C = C, while rGO: NaOH 1: 2 contains C-NO2 bond. The XRD results are reinforced by morphological analysis with SEM test and elemental composition with EDX test. Based on SQUID test analysis with variation of Na concentration to rGO, it has an effect on its magnetism and magnetism value increase with Na addition of Na concentration with higher concentration than rGO (M ~ 0.03 emu / g) due to Na element which slightly fill the void of element missing on lattice honeycomb rGO binding of single or double covalent with C.

Item Type: Thesis (Masters)
Uncontrolled Keywords: Na, rGO, SQUID, tempurung kelapa, coconut shell
Subjects: Q Science > QC Physics
Divisions: Faculty of Mathematics and Science > Physics > 45101-(S2) Master Thesis
Depositing User: Niken Sylvia P
Date Deposited: 31 Oct 2017 04:20
Last Modified: 08 Mar 2019 03:33
URI: http://repository.its.ac.id/id/eprint/44245

Actions (login required)

View Item View Item