Analisis Studi Eksperimen Underwater Welding SMAW di Lingkungan Laut dengan Variasi Elektroda terhadap Uji Impact

Ziva, Kalila (2017) Analisis Studi Eksperimen Underwater Welding SMAW di Lingkungan Laut dengan Variasi Elektroda terhadap Uji Impact. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 4313100018-Undergraduate_Theses.pdf]
Preview
Text
4313100018-Undergraduate_Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Penelitian ini merupakan eksperimen terhadap perbandingan elektroda yang berbeda yaitu AWS E6013 dan AWS E6010 pada lingkungan yang berbeda yakni pengelasan darat dan pengelasan bawah air pada plat baja ASTM A36. Penelitian ini akan membandingkan hasil dari pengujian impact, tarik, kekerasan serta foto struktur makro dan mikro. Dari hasil penelitian didapat bahwa pada pengelasan bawah air dengan elektroda E6013 memiliki sifat yang lebih getas dan tangguh dibanding pengelasan dengan E6010. Hasil uji impact elektroda E6013 pada weld metal 0.947 J/mm2 dan pada HAZ 1.657 J/mm2. Pada specimen pengelasan bawah air dengan elektroda E6010 memiliki hasil uji impact 0.832 J/mm2 pada weld metal dan 1.542 J/mm2 pada HAZ. Pada pengelasan darat elektroda E6010 memiliki sifat yang lebih getas dan keras dibanding dengan elektroda E6013 tetapi memiliki nilai uji impact yang rendah. Elektroda E6013 memiliki hasil uji impact darat 1.213 J/ mm2 pada weld metal dan 1.577 J/ mm2 pada HAZ. Dan elektroda E6010 0.793 J/ mm2 pada weld metal dan 1.383 J/ mm2 pada HAZ.

==========================================================

This research is an experiment on different electrode comparisons AWS E6013 and AWS E6010 in different environments for surface welding and underwater welding on steel plate ASTM A36. This study will compare the results of impact, tensile, hardness, macro and micro structure test. Results from the research found that the underwater welding with E6013 electrode has a more brittle and tough structure than welding with E6010. Test results from the impact test shows that underwater welding using electrode E6013 on weld metal 0.947 J/mm2 and at HAZ 1,657 J/mm2. For speciments of electrode E6010 in underwater welding has porosity defects making the results not optimum. For the on land welding the usage of electrode E6010 has a more brittle and hard properties compared with E6013 electrode but it has a low impact test value. The E6013 electrode has an average impact test of 1.213 J/mm2 on weld metal and 1,577 J/mm2 on HAZ. And E6010 electrode has an average value of 0.793 J/mm2 on weld metal and 1,383 J/mm2 on HAZ.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: SMAW; Underwater Welding; SMAW; Impact Test
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TC Hydraulic engineering. Ocean engineering > TC1680 Offshore structures
V Naval Science > VM Naval architecture. Shipbuilding. Marine engineering
Divisions: Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User: Kalila Ziva .
Date Deposited: 10 Aug 2017 02:20
Last Modified: 08 Mar 2019 03:16
URI: http://repository.its.ac.id/id/eprint/45239

Actions (login required)

View Item View Item