Analisis Specific Surface Area Dan Kapasitas Massa Aktif Elektroda Plat Positif Lead-Acid Battery Variasi Dua Produsen Berbeda

Ardiyan, Irvan (2017) Analisis Specific Surface Area Dan Kapasitas Massa Aktif Elektroda Plat Positif Lead-Acid Battery Variasi Dua Produsen Berbeda. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2113100142_Undergraduate_Theses.pdf]
Preview
Text
2113100142_Undergraduate_Theses.pdf - Published Version

Download (1MB) | Preview

Abstract

Specific surface area massa aktif pada elektroda aki memengaruhi performa dari elektroda. Active specific surface area dari material elektroda yang terekspos elektrolit yang berada disekelilingnya berbanding lurus dengan jumlah kapasitas yang dapat dicapai saat proses discharge dan charge terjadi. Peningkatan Specific surface area pada masa aktif dapat meningkatakan laju discharge dengan cara meningkatkan laju penetrasi larutan elektrolit yang dapat bereaksi dengan porous active material bagian dalam pada elektroda dan membantu proses difusi H2O dan H2SO4. Perbedaan pada komposisi pasta, proses curing, proses soaking dan proses forming akan memengaruhi besar Specific surface area dari massa aktif elektroda aki. Dengan adanya perbedaan Specific surface area dari massa aktif maka akan diikuti oleh perbedaan performa elektroda salah satunya adalah kapasitas karena semakin besar Specific surface area dari massa aktif maka semakin besar juga jumlah massa aktif yang terlibat dalam reaksi kimia yang terjadi.
Metode penelitian diawali dengan mengukur Specific Surface Area dari 2 spesimen plat yang diproduksi oleh 2 produsen yang berbeda yang dijadikan sampel dengan metode BET Specific Surface Area Measurement Technique. Dari pengujian tersebut akan didapatkan besar Specific Surface Area dengan satuan m2 per-gram massa dari tiap-tiap sampel yang diuji. Lalu dibandingkan agar diketahui mana plat yang memiliki Specific surface area lebih tinggi dan mana plat yang memiliki Specific surface area lebih rendah. Setelah mengethui hal tersebut maka setiap plat diuji kapasitas pada proses charge dan discharge dengan alat Potentiostat/Galvanostat dengan prosedur chrono charge discharge galvanostatic. Hasil dari pengujian dari alat Ini adalah besar kapasitas dari plat dengan satuan mAh.
Hasil yang didapatkan dari penelitian ini adalah hubungan antara Specific surface area massa aktif dan kapasitas massa aktif plat aki pada proses charge dan discharge dengan variasi produsen pada plat positif elektroda aki yang kemudian hari dapat digunakan untuk penelitian lebih lanjut dan pembuatan prototype aki yang digunakan untuk deep discharge rate.
=========================================================
Specific surface area of active mass on lead acid battery affect the performance of the electrodes. Active specific surface area of the electrodes material that exposed to electrolyte on its surrounding increase linearly with capacity that it can achive on charge and discharge processes. Increase of specific surface area in active mass can increase the penetration rate electrolyte solution which can react with porous active material inside of the electrodes and sustain the H2O and H2SO4¬ diffusion process. The difference in paste composition, curing process, soaking process and forming process will affect the specific surface area of electrodes active mass. With the difference in specific surface area of active mass the performance will also diffrent, one of which is capacity. The bigger the specific surface area of the active mass, more of the active mass will involved in the chemical reaction.
The research method started with analyzing specific surface area of 2 plate specimen that produced by 2 different manufacturer that have taken as sample with BET Specific Surface Area Measurement Method. From that analysis the specific surface area will be determined in m2/g mass of each tested sample. And then concluded which positive plate that have bigger specific surface area than the other. After that every plate is again tested for its capacity while undergoes charge and discharge processes with Potentiostat/Galvanostat device with chrono charge discharge as the testing procedure. From this analysis capacity of each positive plate will be determined in mAh.
The result of this research is the relation between specific surface area of the active mass and the capacity of the lead acid positive plate active mass which in the future can be used in further reaserch and deep discharge rate lead-acid battery prototyping.

Item Type: Thesis (Undergraduate)
Additional Information: RSM 621.312 42 Ard a
Uncontrolled Keywords: Aki, Massa Aktif, Specific Surface Area, Kapasitas
Subjects: T Technology > TP Chemical technology > TP255 Electrochemistry, Industrial.
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Ardiyan Irvan
Date Deposited: 22 Jan 2018 02:26
Last Modified: 08 Mar 2019 06:26
URI: http://repository.its.ac.id/id/eprint/45618

Actions (login required)

View Item View Item