Uji Kompatibilitas Membran Lapis Ganda NiO/La0, 6Sr0, 4Co0, 2Fe0,8O3-δ (LSCF 6428), NiO/La0,7Sr0,3Co0,2Fe0,8O3-δ (LSCF 7328) dan NiO/La0,7Sr0,3MnO3-δ (LSM 73)

Sahasrikirana, Mutya Sandei (2017) Uji Kompatibilitas Membran Lapis Ganda NiO/La0, 6Sr0, 4Co0, 2Fe0,8O3-δ (LSCF 6428), NiO/La0,7Sr0,3Co0,2Fe0,8O3-δ (LSCF 7328) dan NiO/La0,7Sr0,3MnO3-δ (LSM 73). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1413100011-Undergraduate_Theses.pdf - Published Version

Download (3MB) | Preview

Abstract

Penelitian ini bertujuan untuk mengetahui kesesuaian atau kompatibilitas antara muai panas perovskit La0,6¬Sr0,4Co0,2Fe¬0,8O3-δ (LSCF 6428), La0,7Sr0,3Co0,2Fe¬0,8O3-δ (LSCF 7328) dan La0,7Sr0,3MnO3-δ (LSM 73) dengan NiO untuk dijadikan membran lapis ganda NiO/LSCF 6428, NiO/LSCF 7328 dan NiO/LSM 73. Serbuk perovskit telah berhasil disintesis dengan metode solid state. Pembuatan membran lapis ganda NiO/LSCF 6328, NiO/LSCF 7328 dan NiO/LSM 73 dilakukan dengan metode dry pressing. Sebelumnya dilakukan pembuatan dan karakterisasi membran tunggal LSCF 6428, LSCF 7328, LSM 73 dan NiO. Hasil yang diperoleh menunjukkan bahwa LSCF 7328 memiliki kerapatan tertinggi diikuti oleh LSM 73 dan LSCF 6428. Perbedaan kerapatan tersebut menyebabkan perbedaan pada kekerasan dan muai panas membran tunggalnya. Nilai koefisien muai panas LSCF 6428, LSCF 7328, LSM 73 dan NiO berturut-turut sebesar 22,155; 9,307; 10,135 dan 20,860 10-6.°C-1. Perbedaan/ketidakseuaian nilai muai panas ini menyebabkan delaminasi/keretakan pada membran lapis ganda yang disiapkan dengan metode dry pressing. Oleh karena itu dilakukan penambahan agen perekat berupa amilum pada lapisan perovskit. Penambahan amilum ini berhasil menyebabkan NiO dapat melekat pada lapisan perovskit. ========================================================================================= The aims of this research are to study compatibility assessment about thermal expansion behavior of La0,6-Sr0,4Co0,2Fe¬0,8O3-δ (LSCF 6428), La0,7Sr0,3Co0,2Fe¬0,8O3-δ (LSCF 7328), La0,7Sr0,3MnO3-δ (LSM 73) and NiO to formed double layer membranes NiO/LSCF 6428, NiO/LSCF 7328 dan NiO/LSM 73. Perovskite powder was successfully synthesized by solid state reaction. Double layer membranes NiO/LSCF 6428, NiO/LSCF 7328 and NiO/LSM 73 were fabricated by dry pressing method. Forgoing, single layer membranes of LSCF 6428, LSCF 7328, LSM 73 and NiO were fabricated and characterized. The results showed that LSCF 7328 has the highest density then followed by LSM 73 and LSCF 6428. The difference of density of three single layer membranes also cause the different of hardness and thermal expansion behavior of the membranes. Thermal expansion coefficient (TEC) of LSCF 6428, LSCF 7328, LSM 73 and NiO were 22.155; 9.307; 10.135 and 20.860 10-6.°C-1, respectively. The different/incompatibility of TEC caused delamination or cracking of double layer membranes prepared by dry pressing method. Therefore, the adhesive agent (starch) had to added on perovskite membrane. The addition of this starch succeeds in causing NiO to be attached to the perovskite layer.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 660.284 24 Sah u
Uncontrolled Keywords: Membran lapis ganda, La1-xSrxCo1-yFeyO3-δ, La1-xSrxMnO3-δ, NiO dan Thermal Expansion Coefficient (TEC).
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Mutya Sandei Sahasrikirana
Date Deposited: 02 Nov 2017 02:30
Last Modified: 05 Mar 2019 07:06
URI: https://repository.its.ac.id/id/eprint/48060

Actions (login required)

View Item View Item