Pengaruh Suhu Sintering Terhadap Membran Rapat Asimetris Perovskit La0,6Sr0,4Co0,2Fe0,8O3-δ yang Disiapkan dengan Metode Inversi Fasa

Etriana, Rifka (2017) Pengaruh Suhu Sintering Terhadap Membran Rapat Asimetris Perovskit La0,6Sr0,4Co0,2Fe0,8O3-δ yang Disiapkan dengan Metode Inversi Fasa. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1413100015-Undergraduate_Theses.pdf]
Preview
Text
1413100015-Undergraduate_Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Membran rapat asimetris La0,6Sr0,4Co0,2Fe0,8O3-δ (LSCF 6428) telah disintesis dari oksida perovskit La0,6Sr0,4Co0,2Fe0,8O3-δ yang dibuat dengan metode solid state. Membran dengan struktur asimetris diperoleh dari proses inversi fasa rendam-endap dan tahap sintering dengan polietersulfon sebagai polimer perekat (binder), DMSO sebagai pelarut dan aqua-DM sebagai non-pelarut. Suhu sintering sangat mempengaruhi morfologi akhir membran rapat asimetris. Suhu sintering yang digunakan yaitu 950°C, 1100°C dan 1250°C serta waktu penahanan selama 4 jam dan 8 jam. Fasa kristal LSCF 6428 dianalisa dengan X-Ray Diffraction (XRD) dan menunjukkan kesesuaian dengan data standar International Center Difraction Data oksida perovskit LaCoO3. Foto Scanning Electron Microscope (SEM) menunjukkan bahwa telah terbentuk membran berstruktur asimetris dengan lapisan rapat dan lapisan berpori memanjang (finger like). Kekerasan membran yang diukur dengan Micro Vickers Hardness menunjukkan bahwa membran dengan suhu sintering 1250°C memiliki kekerasan antara 278,9 sampai 488,9 Hv serta menghasilkan membran yang keras dan tidak rapuh. Semakin tinggi suhu sintering membran semakin meningkat pula kerapatan dan kekerasan membran. Selain itu suhu yang lebih tinggi juga menyebabkan penyusutan yang semakin besar dan volume pori yang semakin kecil. Koefisien muai panas membran yang diukur dengan Thermal Mechanical Analysis (TMA) membran yang di sinter pada suhu 950oC memiliki koefisien muai panas paling tinggi dibandingkan dengan yang disinter pada 1250oC dan 1100oC. Selain itu, hasil analisis dengan TMA menunjukkan bahwa pada suhu tertentu, membran mengalami penyusutan yang diperkirakan karena terjadi sintering pada membran.

======================================================================================================

La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF 6428) dense membrane have been synthesized from LSCF 6428 perovskite oxide that was prepared by solid state method. Membrane with asymmetric structure was obtained from phase inversion method and sintering technique with poliethersulfone as polymer binder, DMSO as solvent and aqua-DM as non-solvent. The sintering temperature has significant effect on the morphology of asymmetric dense membrane. These asymmetric dense membrane was sintered at 950°C, 1100°C and 1250°C with holding time 4 hours and 8 hours. Crystal phase of LSCF 6428 was characterized using X-Ray Diffraction (XRD) and the result compatible with standard data of International Center Difraction Data of LaCoO3 perovskit oxide. Scanning Electron Microscope (SEM) photographs shows that dense layers and finger-like layers asymmetric dense membrane has been formed. Membrane hardness that measured with Micro Vickers Hardness show that membrane with sintering temperature 1250°C have hardness value about 278,9 to 488,9 Hv and also obtained strong and not fragile membrane. The higher sintering temperature of membrane increase its density and hardness. Moreover, the higher sintering temperature also lead to increase the shringkage and decrease pore volume. Thermal expansion coefficient of membrane measured with Thermal Mechanical Analysis (TMA). Membrane that sintered at temperature 950oC have the highest thermal expansion coefficient compared to the others. Moreover, Thermal Mechanical Analysis (TMA) result show that at certain temperature membrane was shrink which is expected due to sintering.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Oksida perovskit, La0,6Sr0,4Co0,2Fe0,8O3-δ, Inversi Fasa Rendam-Endap, Membran Asimetris, Suhu Sintering
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis