Pengaruh Penambahan Aditif PEG Terhadap Morfologi Dan Kekuatan Mekanik Membran Asimetris Perovskit La0,6Sr0,4Co0,2Fe0,8O3-δ

Habib, Mohammad Hasnan (2017) Pengaruh Penambahan Aditif PEG Terhadap Morfologi Dan Kekuatan Mekanik Membran Asimetris Perovskit La0,6Sr0,4Co0,2Fe0,8O3-δ. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1413100081-undergraduate_Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Telah dilakukan pembuatan membran asimetris oksida perovskit LSCF 6428 dengan metode inversi fasa rendam-endap dan sintering. Oksida perovskit LSCF 6428 yang digunakan disintesis dengan metode solid state. Pada penelitian ini digunakan poli eter sulfon (PESf) sebagai polimer perekat, dimetil sulfoksida (DMSO) sebagai pelarut dan aqua DM sebagai non-pelarut koagulan. Dilakukan variasi penambahan aditif PEG 6000 dan 8000 dengan masing-masing konsentrasi 0; 0,23%; 0,39% dan 0,55 %. Membran mentah yang dihasilkan diamati morfologinya menggunakan SEM. Membran dengan penambahan aditif PEG 6000 memiliki morfologi yang paling teratur. Semakin besar konsentrasi PEG yang ditambahkan membentuk lapisan rapat yang semakin tipis dan diameter pori berbentuk fingerlike semakin kecil. Selanjutnya dilakukan dekomposisi polimer dan sintering membran mentah pada suhu 1250 °C selama 4 jam. Hasil pengamatan morfologi membran setelah sintering menunjukkan membran menjadi lebih rapat dan ukuran pori mengecil, namun tidak terjadi perubahan yang berarti pada struktur membran asimetris LSCF 6428. Uji kekerasan membran menunjukkan bahwa membran dengan penambahan aditif 8000 memiliki nilai kekerasan lebih besar dibandingkan membran dengan penambahan aditif 6000. ========================================================================================== LSCF 6428 perovskite asymmetric membranes were prepared by phase inversion and sintering methode. LSCF 6428 perovskite which used was synthesized by solid state method. This study used poly ether sulphone (PESf) as binder polymer, dimethyl sulfoxide (DMSO) as solvent and aqua DM as non- solvent or coagulant. Poly Ethylen Glycol (PEG) 6000 and 8000 as additives was added with each concentration of 0; 0,23%; 0,39% dan 0,55 %.The obtained green bodies morphology were observed by SEM. The green bodies with PEG 6000 additive have better uniform morphology than others. Increase PEG concentration reduce dense layer and pore size. Next, the green bodies were sintered at 1250 °C with dwell time of 4 hours. The observation of the sintered membranes morphology showed that the membrane becoming denser and the pore size becoming smaller, but no significant change in the structure of LSCF 6428 asymmetric membrane. LSCF 6428 perovskite asymmetric membranes which added PEG 8000 is harder than PEG 6000 added membranes.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 660.284 24 Hab p
Uncontrolled Keywords: Membran asimetris, LSCF 6428, inversi fasa, aditif PEG
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Mohammad Hasnan Habib
Date Deposited: 02 Nov 2017 02:15
Last Modified: 05 Mar 2019 07:24
URI: https://repository.its.ac.id/id/eprint/48093

Actions (login required)

View Item View Item