Analisa Pengaruh Penambahan Bakelit Terhadap Sifat Fisis Dan Mekanik Komposit Melamina / Ldpe / Pet Sebagai Paving Block Dengan Menggunakan Metode Hot Press

Naweswara, Raka Bayu (2018) Analisa Pengaruh Penambahan Bakelit Terhadap Sifat Fisis Dan Mekanik Komposit Melamina / Ldpe / Pet Sebagai Paving Block Dengan Menggunakan Metode Hot Press. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
02511440000004-Undergraduate-Thesies.pdf - Accepted Version

Download (4MB) | Preview

Abstract

Penelitian ini berisi tentang salah satu metode yang menjanjikan dalam proses pengolahan sampah plastik dan agregat yaitu metode hot press. Jenis sampah plastik yang akan digunakan adalah jenis sampah plastik yang akan dijadikan bahan baku adalah low-density polyethylene (LDPE) dan polyethylene terephtalate (PET) dengan agregat yang dipakai adalah bakelite dan melamine. Produk komposit yang akan dihasilkan dari penelitian ini adalah berupa beton ringan dengan kekuatan sesuai dengan standar SNI. Pengujian yang dipakai untuk mengetahui sifat mekanik dan fisik dari komposit adalah SEM, FTIR, uji kompresi, uji densitas, dan uji absorbsi air. Untuk nilai uji kompresi tertinggi adalah 24.13 Mpa dengan penambahan 15%wt bakelit. Untuk nilai densitas terrendah adalah 1.0042 g/cm3 dengan penambahan 15%wt bakelit. Dengan hasil tersebut paving block yang dihasilkan berkualitas B. ========================================================= Plastic waste has become one of the biggest problem for all people on earth. It’s necessary to develop a process to recycle the waste, especially plastic waste. In this research, we discuss about the recycling process of plastic waste using hot press method. The plastic waste that will be recycled is LDPE, PET, Melamine, and Bakelite. The outcome of this research is paving block based on the National Standard of Indonesia. The material and the product will be tested by SEM, FTIR, density test, compression test, and water absorbability test. For the result, the highest compression stress of the product is 24.13 Mpa for 15%wt added bakelite. The lightest density of the product is 1.0042 gram/cm3 for 15%wt added bakelite. Then, the paving block made by this research has B quality.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Bakelit, LDPE, melamina, PET
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Raka Bayu Naweswara
Date Deposited: 21 Jun 2021 02:14
Last Modified: 21 Jun 2021 02:14
URI: https://repository.its.ac.id/id/eprint/52912

Actions (login required)

View Item View Item