Analisis Pengaruh Variasi Waktu Pencelupan Terhadap Ketebalan Kekerasan Dan Ketahanan Korosi Hasil Elektroplating Nikel Hard Krom Pada Baja AISI 4340

Rachmadi, Mohammad Adnan (2018) Analisis Pengaruh Variasi Waktu Pencelupan Terhadap Ketebalan Kekerasan Dan Ketahanan Korosi Hasil Elektroplating Nikel Hard Krom Pada Baja AISI 4340. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
02511440000116-Undergraduate_Thesis.pdf - Accepted Version

Download (4MB) | Preview

Abstract

Dalam suatu industri manufaktur, terkadang diperlukan logam yang memiliki gabungan sifat dari beberapa jenis logam. Misalnya logam yang memiliki kekerasan yang tinggi tetapi juga tahan terharap korosi. Salah satu metode yang dapat digunakan dengan menggunakan metode elektroplating hard krom, selain dapat melindungi permukaan baja, juga dapat meningkatkan kekerasan permukaan dan sifat ketahanan korosi. Sebelum melakukan pelapisan pada hard krom dilakukan terlebih dahulu menggunakan pelapisan dasar dengan menggunakan nikel. Langkah pertama yang dilakukan metode elektroplating adalah dengan mempersiapkan spesimen dalam hal ini menggunakan baja AISI 4340, kemudian melakukan pemotongan, selanjutnya melakukan pengamplasan spesimen dengan grade 120-500 setelah itu dilakukan proses degreasing dengan menggunakan larutan basa NaOH 35 gram, pada proses ini benda kerja dicelupkan dalam larutan selama ±5 menit dengan temperatur 60o C kemudian dilakukan pembilasan dengan menggunakan aquades pada temperatur kamar, selanjutnya dilakukan proses pickling, larutan ini menggunakan larutan asam yaitu H2SO4 penggunakan dilakukan pada temperatur 50 oC selama 10-15 detik kemudian dilakukan pembilasan dengan aquades dengan cara mencelupkan benda kerja pada temperatur kamar. Kemudian dilakukan elektroplating lapisan dasar dengan menggunakan Nikel yaitu dengan menggunakan larutan Watt’s Bath. Larutan ini terdiri dari 250 g/l NiSO4, 50 g/l NiCl dan 40g/l. Proses ini dilakukan pada rentang rapat arus 1 A/dm2 dan pada rentang temperatur 50 oC. Pelapisan hard chromium merupakan tahap pelapisan terakhir. Dimana pada proses pelapisan ini akan diberlakukan kuat arus 1 Ampere yang mana jenis larutan yang digunakan adalah larutan Chromic Sulfate, yang terdiri dari 250g/l asam kromat (CrO3) dan 2,5 g/l asam sulfat. Proses pelapisan ini dilakukan pada kisaran temperatur 50oC dan waktu pencelupan divariasikan selama 5 menit, 10 menit,15 men it, 20 menit. Pada proses elektroplating hard krom yang menggunakan lapisan dasar nikel didapat kesimpulan bahwa Ketebalan tertinggi berada pada variasi waktu waktu 20 menit 19,95 µm. Nilai kekerasan tertinggi juga terjadi pada variasi waktu 20 menit 526 HVN variasi waktu 20 menit corrosion ratenya terendah 0,040 mm/a. ============================================================================================================ Manufacture industry, required for various properties. For example a metal that has a high hardness but also resistant to corrosion. One method that can be used by using hard chrome electroplating method, can be used, and also can improve endurance. Prior to coating on hard chrome is done first using a base coating using nickel. The first step by electroplating method is to fill the specimen in this case using AISI 4340 steel, then do the cutting, then do the sanding of specimen with grade 120-500 after that done degreasing process by using alkaline NaOH 35 gram solution, in this process workpiece dipped in composition for ± 5 minutes with temperature 60o C so done rinsing by using aquades at room temperature, then carried out the process of preservation, that is using acid solution that is H2SO4 use done at temperature 50 oC for 10-15 second then rinsing with aquades by dipping workpiece at room temperature. Then performed electroplating base layer using Nickel that is by using Watt's Bath solution. This solution consists of 250 g / l NiSO4, 50 g / l NiCl and 40g / l. This process is carried out at a current density range of 1 A / dm2 and at a temperature range of 50 oC. Hard chromium coating is the last part of the final coating. Where in this coating process will be applied a strong flow of 1 Ampere which type used is sulfuric acid, which consists of 250 g / l of chromic acid (CrO3) and 2.5 g / l of sulfuric acid. This coating process is carried out in the 50oC temperature range and the dipping time is varied for 5 minutes, 10 minutes, 15 minutes, 20 minutes. In the hard chrome electroplating process using the base material found that the highest thickness is only once 20 minutes 19.95 μm. The highest hardness value and also occurred at 20 minutes 526 HVN time 20 minute corrosion rate under 0.040 mm / a.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Elektroplatimg, Baja AISI 4340,Elektroplating Nikel, Elektroplating Hard krom
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
T Technology > TP Chemical technology > TP255 Electrochemistry, Industrial.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Mohammad Adnan Rachmadi
Date Deposited: 06 Dec 2018 09:44
Last Modified: 06 Oct 2020 04:24
URI: https://repository.its.ac.id/id/eprint/53296

Actions (login required)

View Item View Item