Analisis Pengaruh Variasi Temperatur dan Waktu Tahan Tempering pada Proses Hardening terhadap Sfat Mekanik dan Struktur Mikro Material Hammer Crusher

., Argyabrata (2018) Analisis Pengaruh Variasi Temperatur dan Waktu Tahan Tempering pada Proses Hardening terhadap Sfat Mekanik dan Struktur Mikro Material Hammer Crusher. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
02511440000109-Undergraduate_Theses.pdf - Accepted Version

Download (5MB) | Preview

Abstract

Clinker Cooler adalah salah satu peralatan yang memiliki fungsi sangat penting dalam industri semen. Clinker cooler berfungsi untuk mendinginkan terak (clinker) yang diproduksi oleh kiln sebelum terak diproses lagi sebagai bahan baku pembuat semen. Terak yang dihasilkan oleh kiln didinginkan di dalam clinker cooler, kemudian ukuran terak tersebut diperkecil dengan hammer crusher yang ada di dalam clinker cooler. Pada prosesnya, hammer crusher yang terdapat di clinker cooler mengalami keausan karena terus menerus mendapat beban berupa clinker yang ukurannya bermacam-macam pada temperatur operasi sekitar 100˚C - 250˚C. Material yang digunakan pada hammer crusher adalah high chromium white cast iron. Dalam penelitian ini, dilakukan analisis kegagalan dari hammer crusher dan solusi dari kegagalan tersebut berupa hardening dan tempering. Pengujian yang dilakukan adalah uji komposisi, uji kekerasan, uji keausan, dan metalografi. Berdasarkan uji komposisi OES dan uji kekerasan, yang menyebabkan kegagalan adalah kesalahan dalam komposisi material dan kekerasan material yang tidak sesuai standar ASTM. Solusi yang ditawarkan dari kegagalan ini yaitu perlakuan panas yang dapat menghasilkan kekerasan yang sesuai dengan standar kekerasan ASTM A532 berupa hardening pada temperatur 1000˚C dan tempering dengan variasi temperatur hardening pada 200˚C, 250˚C, dan 300˚C, serta variasi waktu tahan 2 jam dan 3 jam. Setelah diberi perlakuan panas, nilai kekerasan tertinggi terdapat pada spesimen dengan hardening dan tempering pada temperatur 200˚C dengan waktu tahan 2 jam. Nilai kekerasan yang didapat adalah 699,6 HV, dengan laju keausan sebesar 1,67 mm/jam. Nilai kekerasan berbanding terbalik dengan laju keausan, yang menandakan laju keausan rendah memiliki ketahanan aus yang tinggi. ========================================================================================================= Clinker Cooler is one of the equipment that has a very important function in the cement industry. Clinker cooler has a function to cool the clinker produced by kiln before the slag is processed again as raw material of the cement. The slag produced by the kiln will be cooled in the clinker cooler, and then the size of the slag will be minimized by the hammer crusher in the clinker cooler. In the process, the hammer crusher placed in the clinker cooler is wearable because of continuous clinker loads of varying sizes at operating temperatures around 100˚C - 250˚C. The material used in hammer crusher is high chromium white cast iron. In this research, there is an investigation the cause of failure on hammer crusher and the solution of the failure in the form of hardening and tempering. The tests carried out are composition test, hardness test, wear test, metallography test, and abrasive test. Based on the composition test and hardness test, the factor causing the failure is the error on composition and hardness of material that is not fit with ASTM standard. The solution offered from this failure is heat treatment that can produce hardness in accordance with ASTM A532 hardness standard that is hardening and tempering with variation of hardening temperature at 200˚C, 250˚C, and 300˚C, and variation of holding time at 1 hour and 2 hour each. After heat treatment, the highest hardness values were found in specimen with hardening and tempering at 200°C with 2 hour holding time. The obtained hardness value is 699,6 HV, with wear rate equal to 1,67 mm / hour. The value of hardness is inversely proportional to the wear rate, which signifies the low wear rate has a high wear resistance.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.36 Arg a-1 3100018076477
Uncontrolled Keywords: hammer crusher, high chromium white cast iron, hardening, tempering, ASTM A532
Subjects: T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Mr Argyabrata -
Date Deposited: 13 Aug 2021 04:30
Last Modified: 13 Aug 2021 04:30
URI: https://repository.its.ac.id/id/eprint/53518