Pemanfaatan Limbah Plastik Menjadi Bahan Bakar Dengan Menggunakan Metode Pirolisis dan Penambahan Katalis Zeolit

Pangestu, Alifa Adinda and Robbani, Yusuf (2018) Pemanfaatan Limbah Plastik Menjadi Bahan Bakar Dengan Menggunakan Metode Pirolisis dan Penambahan Katalis Zeolit. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
10411500000018_10411500000096_Non_Degrees.pdf

Download (4MB) | Preview
[img]
Preview
Text
10411500000018_10411500000096_Non_Degrees.pdf

Download (803kB) | Preview

Abstract

ABSTRAK Penggunaan plastik dan barang-barang berbahan dasar plastik semakin meningkat seiring berkembangnya teknologi, industri dan juga populasi penduduk akibat dari peningkatan penggunaan sampah plastik ini adalah bertambah pula sampah plastik. Palstik yang usdah menjadi sampah akan berdampak negatif terhadap lingkungan karena tidak dapat terurai dengan cepat dan dapat menurunkan kesuburan tanah. Oleh karena itu, diperlukan metode yang dapat mengolah sampah namun tidak menimbulkan masalah baru lainnya salah satu metode pengolahan sampah yang telah dikembangkan, yaitu metode pirolisis. Metode pirolisis dapat merubah sampah menjadi bahan bakar. Penelitian ini bertujuan untuk menentukan pengaruh jenis plastik dan penambahan katalis terhadap produk hasil pirolisis. Proses pembuatan bahan bakar dari limbah menggunkan metode pirolisis dengan memotong sampel kemudian mencampur dengan zeolit sesuai variabel yang ditentukan lalu memanasakan tungku pembakaran. Lalu mengambil sampel dari hasil pirolisis setelah itu di analisa kualitas bahan bakar meliputi densitas, viskositas,fire point, nilai kalor . Hasil dari percobaan Pirolisis campuran sampah plastik PET dan PS adalah semakin tinggi suhu pemanasan hasil minyak yang dihasilkan akan semakin banyak zat yang akan terurai menjadi gas dan cair (minyak) Volume terbanyak tanpa penambahan katalis terdapat pada suhu 320 ⁰C yaitu sebanyak 55 mL dan volume terkecil terdapat pada suhu 200 ⁰C yaitu sebanyak 14 mL. Volume terbanyak dengan penambahan katalis terdapat pada suhu 320 ⁰C yaitu sebanyak 51 mL dan volume terkecil terdapat pada suhu 200 ⁰C yaitu sebanyak 11 mL. ========================================================= The use of plastic and plastic-based goods is increasing along with the development of technology, industry and population as a result of increased use of plastic waste is also increasing plastic waste. Palstics that usdah become garbage will have a negative impact on the environment because it can not decompose quickly and can reduce soil fertility. Therefore, a method that can be used to process waste but does not create another new problem one of the methods of waste processing that has been developed, namely pyrolysis method. The pyrolysis method can convert waste into fuel. This study aims to determine the influence of plastic types and the addition of catalysts to pyrolysis products. The process of making fuels from waste uses pyrolysis method by cutting the sample then mixing with zeolite according to the specified variable then cooking the furnace. Then take a sample of pyrolysis results after it dianalisakualitas fuel includes density, viscosity, fire point, value of calor. The results of the PET and PS plastic pyrolysis mixture experiments are the higher the heating temperature of the resulting oil yields the more substances that will decompose into gases and liquids (oil) The highest volume without the addition of catalysts is at 320 ⁰C which is as much as 55 mL and the smallest volume there is at a temperature of 200 ⁰C that is as much as 14 mL. The highest volume with the addition of catalyst is at temperature 320 ⁰C that is as much as 51 mL and the smallest volume is at temperature 200 ⁰C that is as much as 11 mL.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: pyrolysis, catalyst, plastic
Subjects: Q Science > QD Chemistry > QD281 Pyrolysis
Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions: Faculty of Industrial Technology > Chemical Engineering > 24401-(D3) Diploma 3
Depositing User: Alifa Adinda Pangestu
Date Deposited: 05 Jul 2021 10:49
Last Modified: 05 Jul 2021 10:49
URI: https://repository.its.ac.id/id/eprint/56133

Actions (login required)

View Item View Item