Pengaruh Variasi Temperatur Annealing terhadap Sifat Hidrofobik Lapisan SiO2 pada Kaca

Milah, Fasihul (2018) Pengaruh Variasi Temperatur Annealing terhadap Sifat Hidrofobik Lapisan SiO2 pada Kaca. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 01111340000080-Undergraduate_Theses.pdf]
Preview
Text
01111340000080-Undergraduate_Theses.pdf - Accepted Version

Download (4MB) | Preview

Abstract

Silika telah banyak digunakan pada berbagai macam aplikasi dengan ukuran yang berbeda sesuai dengan kebutuhan. Pasir silika telah banyak digunakan sebagai pengisi pada bahan komposit. Penelitian ini bertujuan untuk mengetahui cara mensintesis silika dengan menggunakan metode sol-gel untuk mengetahui pengaruh variasi temperatur pada material lapisan hidrofobik. Bahan yang digunakan adalah silika yang disintesis dengan menggunakan metode sol-gel. Sampel silika dikarakterisasi dengan pengujian XRD, SEM, PSA. Dilakukan proses pelapisan kaca dengan larutan silika. proses annealing dilakukan dengan variasi temperatur. Dari hasil pelapisan kaca dilakukan uji UV-Vis, FTIR, WCA dan SEM. Hasil sintesis silica menunjukkan tingkat kemurnian 90,9 %, serta menghasilkan silika dengan fasa kristobalit dan sudut kontak yang terbentuk dengan variasi temperature 80°C, 100°C, 120°C, dan 140°C memiliki nilai berturut-turut 93.29 ° , 94.31 °, 90.42 °, and 89.42 °.
==========================================================================Silica has been widely used in a variety of applications with different sizes as needed. Silica sand has been widely used as a filler on composite materials. The aim of this research is to know how to synthesize silica by using sol-gel method. To know the influence of temperature variation on hydrophobic coating material. The material used is silica which is synthesized using sol-gel method. Silica samples were characterized by XRD, SEM, PSA testing. Performed a coating process on glass with a silica solution. the annealing process is carried out with temperature variations. From the results of glass coating conducted UV-Vis test, FTIR, WCA and SEM. The results of silica synthesis show a 90.9% purity rate, and produce silica with cristobalite phase and contact angle formed with temperature variations of 80 ° C, 100 ° C, 120 ° C, and 140 ° C having successive values of 93.29 ° , 94.31 °, 90.42 °, and 89.42 °

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Annealing, hidrofobik, silika, sol gel
Subjects: Q Science > QC Physics
Q Science > QC Physics > QC585.75.S55 Silica
Divisions: Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis