Analisa Pengaruh Variasi Arus 90A Dan 100A Terhadap Kekerasan Dan Metalografi Pada Pengelasan Under Water Welding Smaw Dengan Kedalaman 15 cm Menggunakan Material ST 41 Dan Elektrode E7016

Ardiantoro, Aby Antariksa (2018) Analisa Pengaruh Variasi Arus 90A Dan 100A Terhadap Kekerasan Dan Metalografi Pada Pengelasan Under Water Welding Smaw Dengan Kedalaman 15 cm Menggunakan Material ST 41 Dan Elektrode E7016. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
10211400000120 - Aby Antariksa Ardiantoro.pdf - Accepted Version

Download (2MB) | Preview

Abstract

SMAW adalah suatu proses las busur manual dimana panas dari pengelasan dihasilkan oleh busur listrik antara elektroda dengan benda kerja. Bagian ujung elektroda, busur, cairan logam las dan daerah daerah yang berdekatan dengan benda kerja, dilindungi dari pengaruh atmosfer oleh gas pelindung yang terbentuk dari hasil pembakaran lapisan pembungkus elektroda. Perlindungan tambahan untuk cairan logam las diberikan oleh cairan logam flux atau slag yang terbentuk. Pada penelitian ini ,perlakuan yang diberikan oleh peneliti adalah pengelasan dengan Perbandingan Arus 90A dan 100A. Pengelasan dilakukan dengan Underwater Welding metode SMAW(Shielded Metal Arc Welding) pada bahan baja ST 41 dengan filler E 70 16 dengan kampuh V tunggal 60°. kemudian diuji dengan menggunakan metalografi dan kekerasan . Pada hasil pengujian makro etsa didapatkan lebar HAZ terbesar terdapat pada hasil las dengan Arus 100A kedalaman 15cm. Dan untuk hasil pengujian kekerasan Rockwell didapat nilai kekerasan tertinggi pada Arus 90A kedalaman 15 cm dengan nilai kekerasan 99 HRB. Semakin besar arus maka semakin akan menghasilkan lebar HAZ yang besar, jika arus lebih kecil maka nilai kekerasan yang didapatkan semakin besar ==================================================================================================================SMAW is manual welding process where the heat is produced by electric arc between electrode and work piece. Electrode tip, arc, molten metal and weld area protected from atmospheric influences by a shielding gas that formed from the burning of the electrode coating layer. Additional protection for molten metal is provided by molten metal flux or slag. In this research, we used current variation 90A and 100A. Underwater welding SMAW (Shielded Metal Arc Welding) were used as the welding method on material ST 41 steel with E 70 16 filler and 30° V single weld pool. Then, this material was tested with macro etching and hardness. From macro etching test, it is shown that in Electric 100 A current has the widest HAZ where 15 cm depth, the HAZ wide is 6 mm. And for the result on hardness Electric 90A which 15 cm depth the hardness value is 99 HRB.

Item Type: Thesis (Diploma)
Additional Information: RSMI 671.52 Ard a
Uncontrolled Keywords: Pengelasan Under Water, SMAW, Perbandingan Arus 90A dan 100A, Baja ST
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA462 Metal Corrosion and protection against corrosion
Divisions: Faculty of Vocational > Mechanical Industrial Engineering
Depositing User: Aby Antariksa Ardiantoro
Date Deposited: 03 Nov 2020 07:06
Last Modified: 03 Nov 2020 07:06
URI: https://repository.its.ac.id/id/eprint/59257